Iron garnet nanoparticles for cancer radiotherapy and chemotherapy

ABSTRACT

Iron garnet nanoparticles and or iron garnet particles containing various activatable nuclides, such as holmium-165( 165 Ho) and dysprosium-164 ( 164 Dy), are disclosed in this application. The iron garnet (e.g., HoIG and DyIG) nanoparticles and iron garnet particles can prepared using hydroxide co-precipitation methods. In some embodiments, radiosensitizers can be loaded on radioactive magnetic nanoparticles or radioactive iron garnet particle and, optionally, coated with suitable lipid bilayers. Methods of using the disclosed nanoparticles and particles for mediating therapeutic benefit in diseases responsive to radiation therapy are also provided. Another aspect of the invention provides films, electrospun fabrics or bandages coverings for the delivery of radiation to the site of a skin lesion amenable to treatment with radiation (e.g., skin cancers or psoriasis).

CROSS-REFERENCE TO RELATED APPLICATION

This application claims the benefit of U.S. Provisional Application Ser. No. 61/929,394, filed Jan. 20, 2014, the disclosure of which is hereby incorporated by reference in its entirety, including all figures, tables and amino acid or nucleic acid sequences.

This invention was funded with monies awarded by the Texas Medical Research Collaborative (grant number RI6058).

BACKGROUND OF THE INVENTION

Although radionuclides have been used therapeutically for several decades the main concern has been their accumulation in non-target healthy tissues. This problem can be controlled by magnetically targeted delivery of radionuclides nanoparticle carriers with chemotherapeutic agents. Such chemotherapeutic agents loaded radionuclide carriers can be injected to a patient and controlled by external magnetic field for targeted drug delivery and selective radiotherapy. Also incorporating hazardous radionuclides in these carriers can be challenging, the process must be amenable to large amount of radioactivity and radionuclides with short half-lives. Neutron activation of particulates with stable isotopes as a means of producing carriers of radioactive isotopes can overcome these limitations.

Particles for the treatment of cancer in combination with x-ray radiotherapy have been reported. For example a metal oxide such as titanium dioxide, zinc oxide, cerium oxide and mixtures of two or more were doped with rare earth elements. Radioactive holmium-166 loaded poly (L)-lactic acid (PLLA) microspheres have been reported for treatment of liver malignancies. A disadvantage of holmium loaded PLLA microspheres is the limited loading capacity of holmium. The average holmium loading in these microspheres is ˜17% (w/w). ¹⁶⁵Ho and ¹⁶⁴Dy containing magnetic nanoparticles with anticancer drugs can be used for magnetically targeted radiotherapy and chemotherapy at the same time. This application seeks to solve this problem by providing nanoparticles with high drug loading capacity which can provide efficient radiotherapy. In some embodiments, nanoparticles associated with radiosensitizers, as disclosed in this application, are capable of mediating toxic effects when the nanoparticles emit radiation at sub-toxic (subtherapeutic) levels.

BRIEF SUMMARY OF THE INVENTION

Iron garnet particles and iron garnet nanoparticles (np) containing various activatable nuclides, such as holmium-165(¹⁶⁵Ho) and dysprosium-164 (¹⁶⁴Dy) are disclosed in this application. The iron garnet (e.g., HoIG and DyIG) nanoparticles and particles can be prepared using hydroxide co-precipitation methods. In some embodiments, radiosensitizers can be loaded on radioactive magnetic nanoparticles and particles, optionally, coated with suitable lipid bilayers. Methods of using the disclosed particles and nanoparticles for mediating therapeutic benefit in diseases responsive to radiation therapy are also provided. Another aspect of the invention provides films, electrospun fabrics or bandages coverings for the delivery of radiation to the site of a skin lesion amenable to treatment with radiation (e.g., skin cancers or psoriasis).

BRIEF DESCRIPTION OF THE DRAWINGS

The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication, with color drawing(s), will be provided by the Office upon request and payment of the necessary fee.

The following terms may be used interchangably within this application: cis-HoIG and HoIG-cisplatin; carbo-HoIG and HoIG-carboplatin; and oxa-HoIG and HoIG-oxaliplatin.

FIGS. 1A-1B. PXRD pattern of (FIG. 1A) HoYIG powder (FIG. 1B) DyYIG powder.

FIGS. 2A-2B. PXRD pattern of (FIG. 2A) HoIG powder (FIG. 2B) Fe₅Ho₃O₁₂; JCPDS 00-023-0282.

FIGS. 3A-3B. PXRD pattern of (FIG. 3A) DyIG powder (FIG. 3B) Fe₅Dy₃O₁₂; JCPDS 01-073-1378.

FIG. 4. Digital images of HoYIG, DyYIG, HoIG and DyIG powder attracted to a magnet.

FIG. 5. Magnetic hysteresis loops of the synthesized HoYIG at room temperature.

FIG. 6. FTIR spectra of HoIG nanoparticles, cisplatin and cisplatin loaded HoIG nanoparticles.

FIG. 7. FTIR spectra of DOPC, cisplatin and cisplatin loaded HoIG nanoparticles.

FIG. 8. Zeta potential vs. pH.

FIG. 9. FTIR spectra of carboplatin, HoIG nanoparticles and carboplatin loaded HoIG nanoparticles.

FIG. 10. FTIR spectra of DOPC, carboplatin and carboplatin loaded HoIG nanoparticles.

FIG. 11 shows the zeta potential vs. pH curves for HoIG, carboplatin loaded HoIG and DOPC coated carboplatin loaded HoIG nanoparticles.

FIGS. 12A-12B. Cumulative release of (FIG. 12A) cisplatin (FIG. 12B) carboplatin.

FIGS. 13A-13C. Platinum release profiles from cis-HoIG (FIG. 13A), carbo-HoIG (FIG. 13B) and oxa-HoIG (FIG. 13C).

FIGS. 14A-14D. A549 cells treated with HoIG, cis-HoIG or cis for 24 h at 37° C. in 5% CO₂. Each well contained 5,000 cells at t=0, and were treated 24 h later. Nanoparticles were made radioactive prior to treatment via neutron-activation. The ratio of [Pt] to radioactivity used in the platinum-containing nanoparticles was ˜80 μM/μCi.

FIGS. 15A-15F. Survival of NSCLC A549 cells treated with carbo-HoIG, oxa-HoIG, carbo and oxa for 24 h at 37° C. in 5% CO₂. Each well contained 5,000 cells at t=0, and were treated 24 h later. Nanoparticles were made radioactive prior to treatment via neutron-activation. The ratio of [Pt] to radioactivity used in the platinum-containing nanoparticles was ˜40 μCi.

FIGS. 16A-16F. ¹⁶⁶Ho-containing electrospun polymer nanofibrous mats. Pieces cut from one mat (FIG. 16A) before and after neutron-activation for (FIG. 16B) 0.5 h, (FIG. 16C) 1.0 h, (FIG. 16D) 2.0 h and (FIG. 16E) 4.0 h in a thermal neutron flux of approximately 3.5×10¹² n/cm²·s in a 1 MW nuclear reactor. FIG. 16F shows radioactivity of ¹⁶⁶Ho-nanoparticles (HoIG) and 33% and 50% (w/w) ¹⁶⁶Ho-containing electrospun polymer nanofibrous mats plotted against (1−e^(−λT)).

FIG. 17. Diagram showing homogeneity of ¹⁶⁶Ho-containing electrospun polymer nanofibrous mat. The 0.5 h irradiation samples (1-4) obtained from separate locations of the bandage with holmium (Ho) content labeled for each sample.

FIGS. 18A-18B. PXRD pattern of (FIG. 18A) HoYIG powder (FIG. 18B) Y₃Fe₅O₁₂: JCPDS 00-033-0693.

FIG. 19. SEM images of synthesized HoYIG.

FIG. 20 shows the EDS sum spectrum of Au/Pd coated HoYIG. Based on the EDS results the synthesized HoYIG consist 15.94% Fe, 4.72% Ho, 78.39% 0, and 0.95% Y. Therefore the formulation of the synthesized HoYIG is Ho_(2.6)Y_(0.4)Fe₅O₁₂.

FIG. 21. Magnetic hysteresis loops of the synthesized HoYIG at room temperature.

FIGS. 22A-22B. Digital image of (FIG. 22A) 10% PAN/5% HoYIG electrospun bandage (FIG. 22B) electrospun bandage pick up by a magnet.

FIGS. 23A-23B and 24A-24B. SEM images (FIGS. 23A and 23B) and fiber diameter distributions of 5% HoYIG loaded; (FIGS. 24A and 24B) 10% HoYIG loaded electrospun fiber mats.

FIGS. 25A-25C. PXRD pattern of (FIG. 25A) HoYIG powder (FIG. 25B) 10% PAN/5% HoYIG electrospun fiber; (FIG. 25C) Y₃Fe₅O₁₂: JCPDS 00-033-0693.

FIG. 26 shows the room temperature magnetic hysteresis loops of the electrospun bandages. Magnetization values have been normalized to the mass of magnetic material. The saturation magnetization (M_(s)) increases as the loading of HoYIG nanoparticle increases. The M_(s) values are 2.5 and 3 emu/g for 5% and 10% HoYIG loaded electrospun bandages respectively (FIG. 7). The noticeably lower values in the saturation magnetization relative to the bulk powder could be ascribed to the low concentration of the garnet magnetic material inside the fibers.

FIGS. 27 a-27 b. PXRD pattern of (a) HoIG powder (b) Fe₅Ho₃O₁₂; JCPDS 00-023-0282.

FIGS. 28 a-28 b show TEM images of as synthesized HoIG nanoparticle.

FIG. 29 shows M-H hysteresis loop of the synthesized HoIG.

FIG. 30 shows the platinum drugs and possible ligand interaction with the HoIG.

FIG. 31. Zetapotential measurements of (a) HoIG, (b) HoIG-cisplatin, (c) HoIG-carboplatin and (d) HoIG-oxaliplatin.

FIG. 32. In vitro release kinetics of encapsulated Pt(IV) compound (a) HoIG-cisplatin, (b) HoIG-carboplatin and (c) HoIG-oxaliplatin in SBF (pH 7.3).

FIGS. 33 a-33 e. Percent cell survival versus radioactivity or Pt concentration in NSCLC A549 cells. The cells were exposed to free Pt drugs (cisplatin or oxaliplatin), blank ¹⁶⁶HoIG or Pt drug-loaded radioactive nanoparticles for 24 h. The ratio of [Pt] to radioactivity used in all the platinum-containing nanoparticles was ˜80 μM Pt/μCi.

FIG. 34. Percent cell survival versus radioactivity or Pt concentration in NSCLC A549 cells with a higher Pt concentration to radioactivity ratio. The cells were exposed to ¹⁶⁶HoIG-cisplatin for 24 h. The ratio of [Pt] to radioactivity used in the platinum-containing nanoparticles was ˜230 μM/μCi.

FIG. 35. Ratio of percent weight metal in tumor to liver after i.v. injection of HoIG-cisplatin.

FIG. 36. Tumor volume ratio after i.v. injection of ¹⁶⁶HoIG-cisplatin and HoIG-cisplatin with magnets.

FIGS. 37A-37B. Nitric oxide (NO) release from (FIG. 37A) nanoparticles and (FIG. 37B) mats containing ¹⁶⁵Ho. Temperature controlled NO-releasing materials have been constructed. FIG. 37A shows release of NO from nanoparticles (AMS np) and FIG. 37B shows release of NO from bandages containing ¹⁶⁵Ho (HoIG-AN/VIM). These materials need further optimization and study; however, FIG. 37B does demonstrate that NO and ¹⁶⁵Ho can be incorporated into one construct. Furthermore, NO can be released over the 24 h period that tumors will be exposed to the bandage, FIG. 37B, after heat-activation.

DETAILED DISCLOSURE OF THE INVENTION

As used herein, the terms “a” or “an” or “the” may refer to one or more than one. For example, “a” marker can mean one marker or a plurality of markers.

As used herein, the term “about,” when used in reference to a measurable value such as an amount of mass, dose, time, temperature, and the like, is meant to encompass variations of ±10%, ±5%, ±1%, ±0.5%, or even ±0.1% of the specified amount.

As used herein, the term “activatable nuclide” refers to non-radioactive atom that may be activated to produce a radionuclide. For example, the disclosed iron garnet nanoparticles and particles can be prepared using nuclides (e.g., holmium dysprosium, lanthanum, praseodymium, samarium and/or rhenium) that become activated by neutron irradiation. Certain embodiments provide for iron garnet nanoparticles and iron garnet particles that contain holmium, dysprosium and yttrium. Other embodiments provide for iron garnet nanoparticles and iron garnet particles that do not contain yttrium (e.g., the iron garnet nanoparticles contain various lanthanides that can be activated by neutron irradiation with the provision that the iron garnet nanoparticles do not contain yttrium). Various other embodiments provide for the omitting one or more of the aforementioned nuclides (e.g., holmium dysprosium, lanthanum, praseodymium, samarium and/or rhenium) from iron garnets particles and nanoparticles formed according to this disclosure where the iron garnets are formed with a combination of lanthanides. The following table provides examples of activatable nuclides and the corresponding radionuclide.

Activatable nuclide Radionuclide Yttrium-89 Yttrium-90 Lanthanum-139 Lanthanum-140 Praseodymium-141 Praseodymium-142 Samarium-152 Samarium-153 Dysprosium-164 Dysprosium-165 Holmium-165 Holmium-166 Rhenium-185 Rhenium-186 Rhenium-187 Rhenium-188

As used herein, the term “and/or” refers to and encompasses any and all possible combinations of one or more of the associated listed items, as well as the lack of combinations when interpreted in the alternative (“or”).

As used herein, the term “cancer” refers to any benign or malignant abnormal growth of cells. Examples include, without limitation, breast cancer, prostate cancer, lymphoma, skin cancer, pancreatic cancer, colon cancer, melanoma, malignant melanoma, ovarian cancer, brain cancer, primary brain carcinoma, head-neck cancer, glioma, glioblastoma, liver cancer, bladder cancer, non-small cell lung cancer, head or neck carcinoma, breast carcinoma, ovarian carcinoma, lung carcinoma, small-cell lung carcinoma, Wilms' tumor, cervical carcinoma, testicular carcinoma, bladder carcinoma, pancreatic carcinoma, stomach carcinoma, colon carcinoma, prostatic carcinoma, genitourinary carcinoma, thyroid carcinoma, esophageal carcinoma, myeloma, multiple myeloma, adrenal carcinoma, renal cell carcinoma, endometrial carcinoma, adrenal cortex carcinoma, malignant pancreatic insulinoma, malignant carcinoid carcinoma, choriocarcinoma, mycosis fungoides, malignant hypercalcemia, cervical hyperplasia, leukemia, acute lymphocytic leukemia, chronic lymphocytic leukemia, acute myelogenous leukemia, chronic myelogenous leukemia, chronic granulocytic leukemia, acute granulocytic leukemia, hairy cell leukemia, neuroblastoma, rhabdomyosarcoma, Kaposi's sarcoma, polycythemia vera, essential thrombocytosis, Hodgkin's disease, non-Hodgkin's lymphoma, soft-tissue sarcoma, osteogenic sarcoma, primary macroglobulinemia, and retinoblastoma. In some embodiments, the cancer is selected from the group of tumor-forming cancers.

As used herein, the terms “increase” and “enhance” (and any grammatical variants of these terms) refer to an increase in the specified parameter of at least about 1%, 2%, 3%, 4%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, 100%, 125%, 150%, 175%, 200%, 250%, 300% or more. For example, radiosensitizers, such as cisplatin, oxaliplatin and carboplatin increase the toxic effects of activated HoIG nanoparticles disclosed herein.

As used herein, the terms “inhibit” and “reduce” (and any grammatical variants of these terms) refer to a decrease in the specified parameter of at least about 1%, 2%, 3%, 4%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, 95%, 99% or more.

As used herein, the term “nanoparticle” (and any grammatical variant thereof) refers to a particle that is about 0.1 nm to about 200 nm in diameter. The term “particle” (and any grammatical variant thereof) refers to iron garnet particles that are between about 0.1 nm and 1 μm in diameter. In some embodiments, the nanoparticle has a diameter of from about 5 nm to about 100 nm or from about 5 nm to about 200 nm. In some embodiments, the particle or nanoparticle is about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 100, 125, 150, 175, 200, 225, 250, 275, 300, 325, 350, 375, 400, 425, 450, 475, 500, 550, 600, 650, 700, 750, 800, 850, 900, 950, 975 or 999 nm in diameter. Particles and nanoparticles disclosed herein refer to iron garnet nanoparticles (IG np) or iron garnet particles into which particular lanthanide nuclides are complexed. These particles and nanoparticles may be made with yttrium, holmium, lanthanum, praseodymium, samarium, rhenium and/or dysprosium dispersed within the iron garnet. Certain embodiments provide for iron garnet nanoparticles or iron garnet particles that contain holmium, dysprosium and yttrium. Other embodiments provide for iron garnet nanoparticles or iron garnet particles that do not contain yttrium (e.g., the iron garnet nanoparticles or iron garnet particles contain various lanthanides that can be activated by neutron irradiation with the provision that the iron garnet nanoparticles do not contain yttrium). Various other embodiments provide for the omitting one or more of the aforementioned activatable nuclides (e.g., holmium dysprosium, lanthanum, praseodymium, samarium and/or rhenium) from iron garnets formed according to this disclosure where the iron garnets are formed with a combination of lanthanides.

In some embodiments, the disclosed iron garnet nanoparticles or iron garnet particles are treated with materials that are “radiosensitizers”. Radiosensitizer compounds are drugs that act in combination with radiation to produce improved response, usually by making DNA more susceptible to radiation, or extending the life of free radicals produced by the radiation. Another type of radiation enhancer includes elements or compounds that interact directly with the radiation to cause more tissue damage by increasing the absorption or scattering of the radiation, causing more local energy deposition by production of secondary electrons, alpha particles, Auger electrons, ionizations, fluorescent photons, and free radicals, for example. For cancer therapy, the purpose is to selectively enhance dose to the tumor, so these drugs, elements or compounds must be preferentially accumulated in tumor tissue or the tumor tissue must respond in a preferential way, to spare normal tissue. Complexes containing platinum, ruthenium, palladium, iron, cobalt, nickel, copper, rhodium, gold, silver and boron can be used as radiosensitizers in this invention. Some non-limiting examples of radiosensitizers include the platinum complexes cisplatin, oxaliplatin and carboplatin. Iron garnet nanoparticles or iron garnet particles disclosed herein can contain various ratios of radiosensitizers. For example, the particles or nanoparticles can contain the following ranges of activatable nuclide/radionuclide containing IG to radiosensitizer (as a % weight of the nanoparticle): about 40.0% to about 60.0% activatable nuclide/radionuclide containing IG and 0% to about 20% radiosensitizer; about 50.0% to about 60.0% activatable nuclide/radionuclide containing IG and 0% to about 112% radiosensitizer; about 50.0% to about 60.0% activatable nuclide/radionuclide containing IG and about 2.0% to about 7.0% radiosensitizer; about 50.0% to about 60.0% activatable nuclide/radionuclide containing IG and about 2.0% to about 12.0% radiosensitizer. Certain non-limiting examples of activatable nuclide/radionuclide containing IG to radiosensitizers, such as cisplatin, oxaliplatin and carboplatin are: HoIG: about 55.6% Ho, 0% Pt; cis-HoIG: about 53.9% Ho, about 10.3% Pt; carbo-HoIG: about 51.2% Ho, about 3.2% Pt; and oxa-HoIG: about 52.9% Ho, about 2.2% Pt. As used in this paragraph, the term “activatable nuclide/radionuclide” is used to indicate the weight percent of a nuclide containing IG or the weight percent of a radionuclide containing IG with respect to a radiosensitizer.

Nanoparticles or particles as disclosed herein can be, optionally, be coated with a lipid or phospholipid. The terms “lipid” and “phospholipid”” (and any grammatical variants thereof), as used herein, refers to any of the numerous lipids that contain a diglyceride, a phosphate group, and a simple organic molecule such as choline. Examples of phospholipids include, but are not limited to, phosphatidic acid (phosphatidate) (PA), phosphatidylethanolamine (cephalin) (PE), phosphatidylcholine (lecithin) (PC), phosphatidylserine (PS), and phosphoinositides which include, but are not limited to, phosphatidylinositol (PI), phosphatidylinositol phosphate (PIP), phosphatidylinositol bisphosphate (PIP2) and phosphatidylinositol triphosphate (PIP3). Additional examples of PC include DDPC, DLPC, DMPC, DPPC, DSPC, DOPC, POPC, DRPC, and DEPC as defined in the art. Phospholipids or lipids used to coat the disclosed IG nanoparticles can be functionalized with various agents, such as polyethylene glycol (PEG) for form pegylated lipids or pegylated phospholipids. Various targeting agents, as disclosed herein, can then be covalently attached to functionalized lipids and/or phospholipids (e.g., pegylated lipids and/or phospholipids) to facilitate targeting of the IG nanoparticles to a specific cell (e.g., a cancer cell).

In some embodiments, the disclosed or iron garnet particles and iron garnet nanoparticles are used at doses that emit “subtherapeutic” levels of radiation. As used herein, the term “subtherapeutic” (and any grammatical variant thereof) refers to levels of radiation that minimally effect the viability of the treated cells. In these embodiments, the viability of the treated cells is reduced by 15% or less. However, when the disclosed IG nanoparticles or IG particles that emit “subtherapeutic” levels of radiation are used in combination with a radiosensitizer, cell viability is decreased by at least 15%, at least 20%, at least 25%, at least 30%, at least 35%, at least 40%, at least 45%, at least 50%, at least 55%, at least 60%, at least 65%, at least 70%, at least 75%, at least 80%, at least 85%, at least 90%, at least 95% or at least 97% and the therapeutic effects of the particles of nanoparticles emitting subtherapeutic levels of radiation is increased or enhanced as described above. Other embodiments provide for a cell viability decrease of between 20% and 80% when IG nanoparticles or IG particles emitting subtherapeutic levels of radiation are used in combination with a radiosensitizer.

As used herein, “pharmaceutically acceptable” means that the material is suitable for administration to a subject and will allow desired treatment to be carried out without giving rise to unduly deleterious side effects. The severity of the disease and the necessity of the treatment are generally taken into account when determining whether any particular side effect is unduly deleterious.

As used herein, the term “radiotherapeutic nanoparticle” refers to a nanoparticle that emits radiation. As used herein, the term “radiotherapeutic particle” refers to a particle that emits radiation. The term “radionuclide” refers to an atom with an unstable nucleus, which undergoes radioactive decay and emits gamma rays and/or other subatomic particles (e.g., beta particles). ¹⁶⁶Ho and ¹⁶⁵Dy are examples of such radionuclides (see, also, the table provided above for additional examples of radionuclides). In certain embodiments, the radiotherapeutic nanoparticles and/or radiotherapeutic particles are activated by neutron irradiation such that the nanoparticles or particles emit low “subtherapeutic” levels of radiation, and have little to no effect to cell surrounding the location of the nanoparticles. In other embodiments, the radiotherapeutic nanoparticles and/or radiotherapeutic particles are irradiated/activated with neutron irradiation such that therapeutic levels of radiation (are emitted by the radiotherapeutic nanoparticle.

As used herein, the term “subject” (and grammatical variants thereof) refers to mammals, avians, reptiles, amphibians, or fish. Mammalian subjects may include, but are not limited to, humans, non-human primates (e.g., monkeys, chimpanzees, baboons, etc.), dogs, cats, mice, hamsters, rats, horses, cows, pigs, rabbits, sheep and goats. Avian subjects may include, but are not limited to, chickens, turkeys, ducks, geese, quail and pheasant, and birds kept as pets (e.g., parakeets, parrots, macaws, cockatoos, and the like). In particular embodiments, the subject is from an endangered species. In particular embodiments, the subject is a laboratory animal. Human subjects may include neonates, infants, juveniles, adults, and geriatric subjects.

As used herein, the term “therapeutically effective” refers to some improvement or benefit to the subject. Alternatively stated, a “therapeutically effective amount” is an amount that will provide some alleviation, mitigation, or decrease in at least one clinical symptom in the subject (e.g., reduced tumor size, decreased incidence of metastasis, etc. for subjects having a form of cancer). Those skilled in the art will appreciate that the therapeutic effects need not be complete or curative, as long as some therapeutic benefit is provided to the subject. The concentration of stable activatable particle (or nanoparticle) and/or radiotherapeutic agent in the pharmaceutical composition may vary widely (i.e., from less than about 0.05% to about 90% or more by weight) in accordance with the particular mode of administration, the disease(s)/disorder(s)/symptom(s) being treated, the age/weight of the subject, etc.

As used herein, the terms “treatment,” “treat,” and “treating” refer to providing a subject with the particles and/or nanoparticles disclosed herein in an effort to alleviate, mitigate, or decrease at least one clinical symptom in the subject. As is apparent to those skilled in the art, the disclosed iron garnet nanoparticles and iron garnet particles can be guided to a target site by magnetic manipulation.

The present invention provides radiotherapeutic nanoparticles and radiotherpaeutic particles. In particular embodiments, the present disclosure provides iron garnet nanoparticles or iron garnet particles that contain an activatable nuclide, such as holmium and/or dysprosium. Thus, one aspect of the invention provides a stable activatable iron garnet nanoparticle or particle comprising, consisting essentially of or consisting of an activatable nuclide precursor. A further aspect of the invention provides a pharmaceutical composition comprising, consisting essentially of or consisting of the disclosed iron garnet nanoparticles and/or iron garnet particle and a pharmaceutically acceptable carrier.

As used herein, the term “pharmaceutically acceptable carrier” refers to any suitable pharmaceutical diluent and/or excipient (for example, phosphate buffered saline and/or isotonic saline solution. Other examples of pharmaceutically acceptable carriers, diluents and excipients may be found, for example, in ANSEL'S PHARMACEUTICAL DOSAGE FORMS AND DRUG DELIVERY SYSTEMS (9th Ed., Lippincott Williams and Wilkins (2010)), PHARMACEUTICAL SCIENCES (18th Ed., Mack Publishing Co. (1990) or REMINGTON: THE SCIENCE AND PRACTICE OF PHARMACY (21st Ed., Lippincott Williams & Wilkins (2005)).

The pharmaceutical composition may also contain various other materials, such as pH adjusting and/or buffering agents, tonicity adjusting and/or buffering agents and lipid-protective agents (e.g., agents that that protect lipids against free-radical damage, such as alpha-tocopherol). The pharmaceutical composition may be formulated so as to be suitable for administration via any known method, including, but not limited to, oral, intravenous (i.v.), subcutaneous, intramuscular, intrathecal, intraperitoneal (i.p.), intra-arterial, intratumoral, intrarectal, intravaginal, intranasal, intragastric, intratracheal, sublingual, transcutaneous and intrapulmonary.

The present invention provides methods of treating a disorder responsive to radiotherapeutic treatment comprising administering to said subject a therapeutically effective amount of a radiotherapeutic nanoparticle and/or a radiotherapeutic particle (optionally in the form of a pharmaceutical composition) of the present invention. In some embodiments, the radiotherapeutic nanoparticle or radiotherapeutic particle is an iron garnet nanoparticle or particle, such as HoIG or DyIG. The radiotherapeutic nanoparticle or radiotherapeutic particle may be administered using any suitable method known in the art, including, but not limited to, oral, intravenous (i.v.), subcutaneous, intramuscular, intrathecal, intraperitoneal (i.p.), intra-arterial, intratumoral, intrarectal, intravaginal, intranasal, intragastric, intratracheal, intratumoral, sublingual, transcutaneous and intrapulmonary. In some embodiments, the radiotherapeutic agent (radiotherapeutic nanoparticles and/or radiotherapeutic particle) is administered via intraperitoneal injection. In other embodiments, the radiotherapeutic agent is injected directly into a tumor. Yet other embodiments permit the use of a magnet to target or guide the disclosed radiotherapeutic nanoparticles and/or radiotherapeutic particles to a target site. Where targeting agents are associated with the disclosed IG nanoparticles or IG particles, such targeting agents provide a means for guiding the IG nanoparticles and/or IG particles to a target tissue or cell (e.g., an anti-CD20 antibody can be used to guide an HoIG or DyIG nanoparticle to a malignant B-cell for the treatment of Hodgkin's lymphoma).

Methods of the present invention may be used to treat any suitable disorder known in the art, including, but not limited to, bacterial infections, viral infections, cancer, trigeminal neuralgia, severe thyroid eye disease, pterygium, pigmented villonodularsynovitis, vascular restenosis, heterotopic ossification and rheumatoid arthritis, synovial osteochondromatosis, synovial chondromatosis and hemathrosis. In some embodiments, the disorder is a hematological cancer, such as acute myeloid leukemia, chronic myeloid leukemia, hairy cell leukemia, lymphoblastic leukemia, lymphocytic leukemia, AIDS-related lymphoma, Burkitt's lymphoma, cutaneous T-Cell lymphoma, Hodgkin lymphoma, Non-Hodgkin lymphoma, primary central nervous system lymphoma or myeloma. In some embodiments, the disorder is a solid cancer, such as anal cancer, basal cell carcinoma, bile duct cancer, bladder cancer, bone cancer, brain cancer (e.g., cerebellar astrocytoma, ependymoma, glioma, medulloblastoma, neuroblastoma, etc.), breast cancer (e.g., metastatic breast cancer), cervical cancer, colon cancer, endometrial cancer, esophageal cancer, eye cancer (e.g., intraocular melanoma, retinoblastoma, etc.), gallbladder cancer, gastrointestinal cancer, heart cancer, kidney cancer (e.g., renal cell carcinoma), laryngeal cancer, lip cancer, liver cancer, lung cancer (e.g., non-small cell lung cancer, small cell lung cancer, etc.), melanoma, mesothelioma, oral cancer, ovarian cancer, pancreatic cancer, parathyroid cancer, peritoneal carcinomatosis, pharyngeal cancer, prostate cancer, rectal cancer, skin cancer (e.g., Merkel cell carcinoma, squamous cell carcinoma, etc.), stomach cancer, throat cancer, thyroid cancer, urethral cancer, uterine cancer, vaginal cancer or vulvar cancer.

Because holmium and dysprosium are also emitters of beta particles, the disclosed nanoparticles find use in methods of identifying or imaging the presence of one or more site of various disorders, including, but not limited to, bacterial infections, viral infections, cancer, trigeminal neuralgia, severe thyroid eye disease, pterygium, pigmented villonodularsynovitis, vascular restenosis, heterotopic ossification and rheumatoid arthritis, synovial osteochondromatosis, synovial chondromatosis and hemathrosis. In some embodiments, the disorder is a hematological cancer, such as acute myeloid leukemia, chronic myeloid leukemia, hairy cell leukemia, lymphoblastic leukemia, lymphocytic leukemia, AIDS-related lymphoma, Burkitt's lymphoma, cutaneous T-Cell lymphoma, Hodgkin lymphoma, Non-Hodgkin lymphoma, primary central nervous system lymphoma or myeloma. In some embodiments, the disorder is a solid cancer, such as anal cancer, basal cell carcinoma, bile duct cancer, bladder cancer, bone cancer, brain cancer (e.g., cerebellar astrocytoma, ependymoma, glioma, medulloblastoma, neuroblastoma, etc.), breast cancer (e.g., metastatic breast cancer), cervical cancer, colon cancer, endometrial cancer, esophageal cancer, eye cancer (e.g., intraocular melanoma, retinoblastoma, etc.), gallbladder cancer, gastrointestinal cancer, heart cancer, kidney cancer (e.g., renal cell carcinoma), laryngeal cancer, lip cancer, liver cancer, lung cancer (e.g., non-small cell lung cancer, small cell lung cancer, etc.), melanoma, mesothelioma, oral cancer, ovarian cancer, pancreatic cancer, parathyroid cancer, peritoneal carcinomatosis, pharyngeal cancer, prostate cancer, rectal cancer, skin cancer (e.g., Merkel cell carcinoma, squamous cell carcinoma, etc.), stomach cancer, throat cancer, thyroid cancer, urethral cancer, uterine cancer, vaginal cancer or vulvar cancer. In this aspect of the invention, various known techniques can be used to image a subject including, but not limited to, magnetic resonance imaging (MRI), X ray computed tomography (CT), Single Photon Emission Computed Tomography (SPECT) and micro-computed tomography (MicroCT).

As would be apparent to those skilled in the art, the IG nanoparticles disclosed in this application are magnetizable and are suitable materials for magnetic drug delivery. Thus, the disclosed nanoparticles can be delivered to specific targets within the body by use of magnetic fields or stationary magnets outside the body. Magnetic nanoparticles are routinely used for the treatment of shallow tumors and have been tested for safety and efficacy in animal and human clinical trials. Thus, the disclosed nanoparticles can be injected into a subject, distributed by the circulatory system, and then captured and concentrated at a desired tumor location by magnetic fields or magnets located near or around the tumor. The disclosed nanoparticles can also be delivered to deep tissue tumor sites, such as the lungs, intestines, and liver, through the use of magnetic fields, such as those disclosed in U.S. Pat. No. 8,579,787 (the disclosure of which is hereby incorporated by reference in its entirety). The '787 patent discloses systems and methods for using magnetic fields to contain and deliver magnetizable therapeutic, diagnostic or prophylactic agents in a target volume within a patient's body, or to move such magnetizable agents through a target volume within a patient's body. As would be apparent to those skilled in the art, any known technique for delivering magnetizable nanoparticles to a target site can be used to deliver the IG nanoparticles disclosed herein.

Yet another aspect of the invention provides for a film, electospun fabric or bandage that is impregnated with IG nanoparticles disclosed herein. As used herein, the term “bandage” (and any grammatical variants thereof) refers to a wound covering into which the disclosed IG nanoparticles have been impregnated. Such coverings can be a patch or film. In some embodiments of this aspect of the invention, a bandage or film is produced by dissolving the disclosed IG nanoparticles and a polymer in a solvent; applying a stable nuclide solution on a release paper by a coater and drying. The film/patch/bandage may then be irradiated with neutrons in a nuclear reactor. Another embodiment of the disclosed invention provides using an electrospinning technique to prepare a ¹⁶⁵Ho and/or ¹⁶⁴Dy nanoparticle loaded nanofibers that can be electrospun into a bandage with uniform particle distribution. Various other techniques for forming such bandages are known in the art (see, for example, U.S. Pat. Nos. 4,946,435 and 6,350,226, each of which is hereby incorporated by reference in its entirety and U.S. Patent Application Publication 2013/0337033 which is also hereby incorporated by reference in its entirety). In various embodiments, nanoparticles that are used in the manufacture of a film, electrospun fabric or bandage can have a size of less than about 500 nm, less than about 400 nm, less than about 300 nm, less than about 200 nm, less than about 100 nm, less than about 50 nm or range in size between from about 5 nm to about 100 nm or from about 5 nm to about 200 nm.

As used herein, the phrases “relatively uniform distribution of said nanoparticles/particles within said film, electrospun fabric or bandage” and “relatively uniform radiation across the surface area of said film, electrospun fabric or bandage” relate to the distribution of the nanoparticles/particles and the emitted radiation from said nanoparticles/particles within the film, electrospun fabric or bandage. In this regard, the variance with respect to the number of nanoparticles or the amount of emitted radiation for a given surface area of the film, electrospun fabric or bandage varies by less than about 30%, less than about 25%, less than about 15%, less than about 10%, less than about 5% or less than about 1%. In certain embodiments, the variance with respect to the number of nanoparticles/particles or the amount of emitted radiation for a given surface area of the film, electrospun fabric or bandage varies by about 0.01% to about 5%, about 0.01% to about 5%, about 0.01% to about 5%, about 0.01% to about 2.5%, about 0.01% to about 1%, about 0.1% to about 5%, about 0.1% to about 2.5%, about 0.1% to about 1%, about 0.05% to about 5% or about 0.5% to about 2.5%.

Various additional embodiments of this aspect of the invention provide for the inclusion of additional wound healing agents within the disclosed bandages. For example, nitrous oxide (NO) can be incorporated into a bandage as disclosed in U.S. Patent Application Publication 2013/0337033. As disclosed therein, bandage and gauze materials (herein also referred to as electrospun fabrics) can be prepared from fibers spun from acrylonitrile-based co- and ter-polymers, such as vinylimidazole, butyl acrylate, isoprene, butadiene, and caprolactam (other polymers are also useful in this regard and known in the art, see, for example, Riccio and Schoenfisch, Chem. Soc. Rev., 2012, 41:3731-3741, which is hereby incorporated by reference in its entirety). Once the polymer is spun into fibers, it is exposed to high pressure of NO, allowing the formation of a NO molecular donor group, a diazeniumdiolate (NONOate). These NONOates release two molar equivalents of NO spontaneously upon exposure to physiological conditions. Other agents that can be included within the bandages disclosed herein include agents such as antibiotics, anti-microbial agents, dialkylcarbamoylchloride, povidone-iodine, silver and growth factors, such as epidermal growth factor (EGF), platelet derived growth factor (PDGF), fibroblast growth factor (FGF), transforming growth factor (TGF-β1), insulin-like growth factor (IGF-1), human growth hormone and granulocyte-macrophage colony-stimulating factor (GM-CSF; see, for example, Boateng et al., J. Pharmaceutical Sciences, 2008, 97:2892-2993, which is hereby incorporated by reference in its entirety, particularly with respect to active ingredients using in wound management at pages 2905-2907). The resulting films, electrospun fabrics and bandages can be used for the treatment of skin conditions amenable to treatment with radiation with the concomitant application of wound healing agents, such as NO. Skin conditions suitable for such treatment include psoriasis, melanomas and other skin cancers. Where the film, electrospun fabric or bandage is used for the treatment of skin cancer, radiosensitizers, such as platinum, ruthenium, palladium, iron, cobalt, nickel, copper, rhodium, gold, silver and/or boron, can also be incorporated within the film, electrospun fabric or bandage and therapeutic or subtherapeutic levels of radiotherapeutic nanoparticles can be used for the treatment of skin cancer. In addition to platinum, ruthenium, palladium, iron, cobalt, nickel, copper, rhodium, gold, silver and/or boron, NO (which also provides benefit as a wound healing agent) can function as a radiosensitizer as well. Alternatively, the radiosensitizers can be incorporated into the nanoparticles used in the manufacture of the film, electrospun fabric or bandage.

It should be understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application and the scope of the appended claims. In addition, any elements or limitations of any invention or embodiment thereof disclosed herein can be combined with any and/or all other elements or limitations (individually or in any combination) or any other invention or embodiment thereof disclosed herein, and all such combinations are contemplated with the scope of the invention without limitation thereto.

All patents, patent applications, provisional applications, and publications referred to or cited herein are incorporated by reference in their entirety, including all figures and tables, to the extent they are not inconsistent with the explicit teachings of this specification.

Following are examples which illustrate procedures for practicing the invention. These examples should not be construed as limiting. All percentages are by weight and all solvent mixture proportions are by volume unless otherwise noted.

Example 1 Nanoparticle Synthesis

Synthesis of Holmium yttrium iron garnet (HoYIG), Holmium iron garnet (HoIG), dysprosium yttrium iron garnet (DyYIG) and dysprosium iron garnet (DyIG) nanoparticles:

A hydroxide co-precipitation method can be used to synthesize HoYIG, HoIG, DyYIG and DyIG nanoparticles. Water soluble salt of holmium, dysprosium, yttrium and iron were mixed in the presence of cationic, anionic, non-ionic surfactant, and/or capping agents and a suitable base were used to precipitate HoYIG and DyYIG. The precipitate can be annealed at high temperature in order to get magnetic crystalline product. Same procedure will be followed without yttrium salt to prepare HoIG and DyIG nanoparticles.

Stoichiometric mixtures (5:1.5:1.5) of 1M nitrates of iron (III) (10 mL), holmium (III) (5 mL), and yttrium (III) (3 mL) were mixed with ethylene glycol (21 mL) at room temperature with stirring. Then 6M NaOH (10 mL) were added dropwise to form the HoYIG precipitate. The product was centrifuged and washed with de-ionized water, then dried at 100° C. overnight. The HoYIG was annealed in air at 900° C. for 3 h. Stoichiometric mixtures (5:1.5:1.5) of 1M nitrates of iron (III) (10 mL), dysprosium (III) (5 mL), and yttrium (III) (3 mL) were used to synthesize DyYIG nanoparticles based on the method described above.

These products were characterized using x-ray diffraction (XRD) on a Rigaku Ultima IV diffractometer using Cu Kα radiation. The average crystallite size of the powders was estimated from corresponding XRD data using Scherrer formula. Scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX) analysis was carried out on Zeiss-LEO model 1530 SEM. The magnetic properties of the garnet nanoparticles and fibers were measured using a superconducting quantum interference device MPMS-XL from Quantum Design.

FIGS. 1, 2 and 3 show the PXRD pattern of synthesized HoYIG, DyYIG, HoIG and DyIG. The crystallite sizes were calculated from the PXRD line broadening of the peak (420) using the Scherrer equation, D_(hkl)=kλ/B cos θ, where D_(hkl) is the particle size in nm, k is a constant (shape factor) with a value of 0.9, B is the width of half maximum, and k is the wavelength of the x rays. The D_(hkl) value of HoYIG, DyYIG, HoIG and DyIG are about 36, 38, 35 and 38 nm respectively. The synthesized HoYIG, DyYIG, HoIG and DyIG nanoparticles were olive green in color and are magnetic as demonstrated by the attraction of the powder to a magnet as shown in FIG. 4.

The magnetization of the synthesized HoYIG, DyYIG, HoIG and DyIG powder was performed at room temperature. Plot of magnetization (M) (normalized to the mass of magnetic material) as a function of magnetic field (H) are shown in FIG. 5. The saturation magnetization (Ms) is defined at the state when an increase in the magnetic field cannot increase the magnetization of the material further and Ms for HoYIG, DyYIG, HoIG and DyIG nanoparticles reached 13, 13, 8, 4.9 emu/g. Approximately 10 mg of dry HoIG was neutron-activated in a 1 MW TRIGA Mark I nuclear reactor in a thermal neutron flux of approximately 3.5×10¹² neutrons/cm²·s for 0.5, 1, 2 or 4 h. Gamma radioactivity was then measured, and activities directly after neutron-activation were determined to be 56.8, 330.7, 833.8 and 1633.6 μCi mg⁻¹, respectively. From this, we calculated that the nanoparticles contained approximately 57.8±26.2% w/w holmium. This correlates with inductively coupled plasma-mass spectrometry (ICP-MS) data, which shows that they contain 35.7% w/w holmium.

Example 2 Platinum (Pt) Drug Loading into Ho Containing Garnet Nanoparticles

Cisplatin (10 mg) was dissolved in 10 mL simulated body fluid solution (SBF; Marques et al., Dissolution Technologies, 2011, 18:15-28). HoIG nanoparticles (30 mg) were added to cisplatin solution and sonicated for 24 h. The cisplatin loaded nanoparticles were collected by centrifugation. The amount of remaining cisplatin in the solution was analyzed using UV/Vis and the amount of cisplatin loaded into HoIG nanoparticles was calculated. The cisplatin loaded HoIG nanoparticles was washed with SBF to remove any unbound cisplatin and product was dried at 80° C. for 8 h. Cisplatin drug loaded HoIG nanoparticles was characterized using FTIR-ATR (Table 2).

TABLE 1 FTIR data for cisplatin and cisplatin loaded HoIG nanoparticles Wave Wave Number/ Number/ cm⁻¹ Cisplatin cm⁻¹ Cisplatin_HoIG np 3201 N—H stretching 3140 N—H stretching (symmetric) (symmetric) 3279 N—H stretching 3245 N—H stretching (asymmetric) (asymmetric) 1538 N—H bending 1480 N—H bending 1294 Twisting and 1258 Twisting and wagging vibrations wagging vibrations of NH₃ of NH₃

The red shifts of N—H stretching wavenumber of cisplatin suggest that bonding of cisplatin to HoIG nanoparticles surface via hydrogen bonding (FIG. 6 and Table 1).

DOPC lipid coating on cisplatin loaded HoIG nanoparticles DOPC lipid (30 mg) was dissolved in 5 mL of chloroform. Cisplatin drug loaded HoYIG nanoparticles (30 mg) were added to DOPC solution and sonicated for 3 h. The solvent was evaporated under slow flow of Ar gas and heated (50° C.) SBF solution (5 mL) was added to above dried powder and sonicated for another 1 h. The DOPC coated cisplatin loaded HoYIG nanoparticles were collected by centrifugation and washed using diethylether to remove excess DOPC. The product was dried at 80° C. for 5 h. DOPC coated cisplatin drug loaded HoIG nanoparticles was characterized using FTIR-ATR. The red shifts of P—O and C═O stretching wavenumber of DOPC suggest that bonding of DOPC to cisplatin via hydrogen bonding (FIG. 7 and Table 2).

TABLE 2 FTIR data for cisplatin, DOPC and DOPC coated cisplatin loaded HoIG nanoparticles Wave Wave Wave Number/ Number/ Number/ cm⁻¹ Cisplatin cm⁻¹ DOPC cm⁻¹ DOPC-_cisplatin_HoYIG np 3201 N—H stretching 3104 N—H stretching (symmetric) (symmetric) 3279 N—H stretching 3180 N—H stretching (asymmetric) (asymmetric) 1538 N—H bending 1515 N—H bending 1294 Twisting and wagging 1265 Twisting and wagging vibrations of NH₃ vibrations of NH₃ 1089 P—O stretching 1020 P—O stretching (symmetric) (symmetric) 1245 P—O stretching 1220 P—O stretching (asymmetric) (asymmetric) 1732 C═O stretching 1720 C═O stretching

FIG. 8 shows the zeta potential vs. pH curves for HoIG, cisplatin loaded HoIG and DOPC coated cisplatin loaded HoIG nanoparticles. The isoelectronic point of HoIG, cisplatin loaded HoIG and DOPC coated cisplatin loaded HoIG are 3.70, 3.90 and 9.40 respectively. The figure also shows that in the pH range of body fluid all these materials are stable since the zeta potential values above +30 mV and below −30 mV.

Carboplatin (5 mg) was dissolved in simulated body fluid solution (SBF) (10 mL). HoIG nanoparticles (30 mg) were added to carboplatin solution and sonicated for 24 h. The carboplatin loaded nanoparticles were collected by centrifugation. The amount of remaining carboplatin in the solution was analyzed using UV/Vis and the amount of carboplatin loaded into HoIG nanoparticles was calculated. The carboplatin loaded HoIG nanoparticles was washed with SBF to remove any unbound carboplatin and product was dried at 80° C. for 8 h. Carboplatin drug loaded HoIG nanoparticles was characterized using FTIR-ATR.

The red shifts of N—H stretching wavenumber of carboplatin suggest that bonding of carboplatin to HoIG nanoparticles surface via hydrogen bonding (FIG. 9 and Table 3). Table 4 provides the weight percentage of Ho and Pt in HoIG, cis-HoIG, carbo-HoIG and oxa-HoIG (determined using inductively coupled plasma-mass spectrometry (ICP-MS)).

TABLE 3 FTIR data for cisplatin and cisplatin loaded HoIG nanoparticles Wave- Wave- number/ number/ cm⁻¹ Carboplatin cm⁻¹ Carboplatin_HoYIG np 3255 N—H stretching 3227 N—H stretching (symmetric) (symmetric) 3134 N—H stretching 3094 N—H stretching (asymmetric) (asymmetric)

TABLE 4 Weight percentage of Ho and Pt in HoIG, cis-HoIG, carbo-HoIG and oxa-HoIG, determined using inductively coupled plasma-mass spectrometry (ICP-MS) Sample Wt % Pt Wt % Ho HoIG 0 55.6 cis-HoIG 10.3 53.9 carbo-HoIG 3.2 51.2 oxa-HoIG 2.2 52.9

DOPC lipid was used to coat carboplatin loaded HoIG nanoparticles. DOPC lipid (30 mg) was dissolved in 5 mL of chloroform. Carboplatin drug loaded HoYIG nanoparticles (30 mg) were added to DOPC solution and sonicated for 3 h. The solvent was evaporated under slow flow of Ar gas and heated (50° C.) SBF solution (5 mL) was added to above dried powder and syndicated for another 1 h. The DOPC coated carboplatin loaded HoYIG nanoparticles were collected by centrifugation and washed using diethylether to remove excess DOPC. The product was dried at 80° C. for 5 h. DOPC coated carboplatin drug loaded HoIG nanoparticles was characterized using FTIR-ATR (Table 5).

TABLE 5 FTIR data for DOPC and DOPC coated cisplatin loaded HoIG nanoparticles Wave- Wave- number/ number/ cm⁻¹ DOPC cm⁻¹ DOPC-_carboplatin_HoYIG np 1089 P—O symmetric 1058 N—H stretching stretching (symmetric) 1245 P—O asymmetric 1219 N—H stretching stretching (asymmetric) 1732 C═O stretching 1714 N—H stretching (asymmetric)

The red shifts of P—O and C═O stretching wavenumber of DOPC suggest that bonding of DOPC to carboplatin via hydrogen bonding (FIG. 10 and Table 4). FIG. 11 shows the zeta potential vs. pH curves for HoIG, carboplatin loaded HoIG and DOPC coated carboplatin loaded HoIG nanoparticles. The isoelectronic point of HoIG, carboplatin loaded HoIG and DOPC coated cisplatin loaded HoIG are 3.70, 4.00 and 8.00 respectively. The figure also shows that in the pH range of body fluid all these materials are stable since the zeta potential values above +20 mV and below −20 mV.

In vitro release of Pt drugs was studied at room temperature in simulated body fluid solution of pH 7.30. FIG. 12 shows the cumulative release of cisplatin and carboplatin with time. DOPC coated cisplatin/carboplatin drug loaded HoIG shows slow release as compared to the cisplatin/carboplatin loaded HoIG nanoparticles. Release profiles are provided in FIG. 13. ICP-MS data was collected before and after modification; before, the nanoparticles contained 33.3% and 8.3% holmium and platinum, respectively, and after modification with DOPC, the nanoparticles contained 13.6% and 3.7% holmium and platinum, respectively.

HoIG with and without platinum complexes (cisplatin (cis); oxaliplatin (oxa); or carboplatin (carbo)) were irradiated in a 1 MW nuclear reactor in a neutron flux of approximately 7.6×10¹² neutrons/cm²·s. The radioactivity of nanoparticles prior to administration to cells was determined using a 2470 WIZARD 2 automatic gamma counter. Studies involving human NSCLC A549 cells were carried out under standard conditions in a humidified, 37° C., 5% CO₂ atmosphere incubator. The culture medium used for A549 cells was minimum essential medium to which had been added 10% fetal calf serum, 100 μg/mL streptomycin, 100 IU/mL penicillin and 2.0 mM L-glutamine. Cells were seeded at 5×10⁴ cells/ml (100 μL/well) in 96-well plates and allowed to grow for 24 h after which time the medium was removed and replaced with medium and drug. After an exposure time of 24 h, the medium with drug was removed and replaced with 100 μL of fresh medium. To each well, 20 μL of CellTiter 96® AQueous One Solution Cell Proliferation Assay (MTS) solution was added. After 2 h incubation with the MTS solution, the absorbance was read at 490 nm using a Synergy™ H1 hybrid multi-mode microplate reader. The percent survival of cells treated by each concentration of drug was calculated using the following equation:

${\% \mspace{14mu} {survival}} = {100 \times \left\lbrack \frac{A_{d} - A_{m}}{A_{c} - A_{m}} \right\rbrack}$

where A_(d) is the absorbance of cells treated with drug, A_(m) is the absorbance of medium alone and A_(c) is the absorbance of cells without treatment. The % survival data was fit to exponential regression and IC₅₀ values calculated.

After neutron-activation irradiation in a nuclear reactor, cis-HoIG had greater toxicity than HoIG and free cisplatin toward NSCLC A549 cells. Also, oxa-HoIG had greater toxicity than HoIG and oxa toward NSCLC A549 cells. Thus, cis and oxa act synergistically with the radioactive Ho, making nontoxic doses of radiation extremely efficacious and toxic to target cells (see FIGS. 14 and 15).

Example 3 Electrospinning of a Nanofibrous Mat

A ¹⁶⁵Ho-containing polymer nanofibrous mat was prepared via electrospinning using ¹⁶⁵Ho-nanoparticles (HoIG) and polyacrylonitrile (PAN). The mat was neutron-activated for 0.5, 1, 2 and 4 h in a thermal neutron flux of approximately 3.5×10¹² n/cm²·s in a 1 MW nuclear reactor. In FIG. 16, the bandage can be seen before and after neutron-activation for 0.5-4 h; the treated material looks similar to control (untreated) material after neutron-activation (0.5-4 h) in appearance. Thus, materials can be impregnated with ¹⁶⁵Ho-nanoparticles to prepare a “radiotherapeutic bandage” that can withstand the high temperatures associated with neutron-activation.

The radioactivities of the treated samples was also satisfactory and it appears that these materials can withstand greater neutron-activation times to achieve even higher radioactivity. For example, after 4 hours of neutron-activation, a radioactivity of 650 μCi/mg of mat was produced; each mat was easily cut into small rectangles that were approximately 6 mg in mass. Thus, it is clear that therapeutic levels of radioactivity can easily be reached with ¹⁶⁵Ho-nanoparticle impregnated wound coverings. The electrospun mats were also analyzed to assess the uniformity of radiation emission. Four samples were obtained from different regions of a mat (see FIG. 17, corresponding to those numbered 1-4 in the diagram). After neutron-activation for 0.5 h the radioactivity was measured and, from this, ¹⁶⁶Ho content determined. Approximately 1 mg of ¹⁶⁶Ho was contained in each sample, and thus the process can homogeneously distribute ¹⁶⁵Ho-nanoparticles throughout the bandage.

Example 4 Synthesis of Holmium Yttrium Iron Garnet (HoYIG) and Dysprosium Yttrium Iron Garnet (DyYIG) Nanoparticle

Stoichiometric mixtures (5:1.5:1.5) of 1M nitrates of iron (III) (10 mL), holmium (III) (5 mL), and yttrium (III) (3 mL) were mixed with ethylene glycol (21 mL) at room temperature with stirring. Then 6M NaOH (10 mL) were added dropwise to form the HoYIG precipitate. The product was centrifuged and washed with de-ionized water, then dried at 100° C. overnight. The HoYIG was annealed in air at 900° C. for 3 h. Stoichiometric mixtures (5:1.5:1.5) of 1M nitrates of iron (III) (10 mL), dysprosium (III) (5 mL), and yttrium (III) (3 mL) were used to synthesize DyYIG nanoparticles based on the method described above.

These products were characterized using x-ray diffraction (XRD) on a Rigaku Ultima IV diffractometer using Cu Kα radiation. The average crystallite size of the powders was estimated from corresponding XRD data using Scherrer formula. Scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX) analysis was carried out on Zeiss-LEO model 1530 SEM. The magnetic properties of the garnet nanoparticles and fibers were measured using a superconducting quantum interference device MPMS-XL from Quantum Design. FIG. 18 shows the PXRD pattern of synthesized HoYIG. As compared to YIG simulated pattern peak positions of HoYIG are mostly similar. The crystallite sizes were calculated from the PXRD line broadening of the peak (420) using the Scherrer equation, D_(hkl)=kλ/B cos θ, where D_(hkl) is the particle size in nm, k is a constant (shape factor) with a value of 0.9, B is the width of half maximum, and λ is the wavelength of the x rays. The D_(hkl) values of HoYIG is about 36 nm.

FIG. 19 shows the SEM image of synthesized HoYIG nanoparticles. The particles have nearly a uniform size distribution and also contained some agglomeration and FIG. 20 shows the EDS sum spectrum of Au/Pd coated HoYIG. Based on the EDS results the synthesized HoYIG consist 15.94% Fe, 4.72% Ho, 78.39% 0, and 0.95% Y. Therefore the formulation of the synthesized HoYIG is Ho_(2.6)Y_(0.4)Fe₅O₁₂.

The magnetization of the synthesized HoYIG powder was performed at room temperature. Plot of magnetization (M) (normalized to the mass of magnetic material) as a function of magnetic field (H) are shown in FIG. 21. The saturation magnetization (Ms) is defined at the state when an increase in the magnetic field cannot increase the magnetization of the material further and Ms for HoYIG nanoparticles reached 17.5 emu/g.

Example 5 Electrospinning of Polymer Solutions with HoYIG and DyYIG Nanoparticles

Acrylonitrile (AN)-based polymers can be made into non-woven fiber mats by use of electrospinning HoYIG nanoparticles were dispersed in dimethylformamide (DMF) at room temperature. Polyacrylonitrile (PAN) was dissolved in 8 mL of DMF. Two solutions were mixed together for electrospinning. A solution with nanoparticles in the range of 5-20% weight/volume was prepared. The solution was then loaded into a syringe with a spinneret needle gauge of 18 to 22. A voltage in the range of 8-20 kV (e.g., 13 kV) is applied to the spinneret. The fibers were collected on a rotating drum. As illustrated in FIG. 22, the bandage is flexible and magnetic (the electrospun bandages can be picked up by a magnet).

SEM images of the electrospun fiber mats with different HoYIG nanoparticles loadings are shown in FIGS. 23A and B. As shown in the histogram the average diameter of nanofibers with standard error values are 208±54 nm and 174±56 nm when the HoYIG loading are 5% and 10% (FIGS. 24A and B). The XRD patterns of the electrospun fibers with 5% loading of HoYIG nanoparticles are shown in FIG. 25 and confirm the presence of HoYIG nanoparticles in nanofibers. FIG. 26 shows the room temperature magnetic hysteresis loops of the electrospun bandages. Magnetization values have been normalized to the mass of magnetic material. The saturation magnetization (M_(s)) increases as the loading of HoYIG nanoparticle increases. The M_(s) values are 2.5 and 3 emu/g for 5% and 10% HoYIG loaded electrospun bandages respectively. The noticeably lower values in the saturation magnetization relative to the bulk powder could be ascribed to the low concentration of the garnet magnetic material inside the fibers.

Example 6 Experimental Section

Chemicals. Holmium (III) nitrate hexahydrate, sodium hydroxide, ethylene glycol, cisplatin, carboplatin, oxaliplatin were purchased from the Aldrich Chemical Co. Iron (III) nitrate hexahydrate was purchased from Acros Organics. All reagents were used as received.

Synthesis of Holmium Iron Garnet Nanoparticles (HoIG).

HoIG was synthesized by modifying a reported procedure (Munaweera et al., 2014). Stoichiometric mixtures (5:3) of 1 M nitrates of iron (III) (5 mL) and holmium (III) (3 mL) were mixed with ethylene glycol (21 mL) at room temperature with stirring. Then, 6 M NaOH (10 mL) was added drop-wise to form the HoIG precipitate. The product was centrifuged and washed with de-ionized water, then dried at 100° C. overnight. The HoIG was annealed in air at 900° C. for 3 h.

Platinum Drug Loaded HoIG Nanoparticles (HoIG-Pt).

HoIG-Pt, i.e. cisplatin, carboplatin and oxaliplatin loaded HoIG (HoIG-cisplatin, HoIG-carboplatin and HoIG-oxaliplatin) were prepared using the same manner as described for HoIG. Then, to a solution containing one of the platinum drugs (5 mg) in water (10 mL) was added HoIG (30 mg), and the mixture was sonicated for 3 h. The Pt drug loaded nanoparticles were then collected by centrifugation. The amount of remaining platinum drug in the solution was analyzed using ultraviolet-visible spectrophotometry (UV/Vis, Shimadzu UV-1601PC), and the amount of drug loaded calculated. The product was then dried at 80° C. for 8 h. The dry HoIG-Pt were then digested in nitric acid at 70° C. for 48 h and Pt content analyzed using inductively coupled plasma-mass spectrometry (ICP-MS, NexION 300D from PerkinElmer).

Study of In Vitro Release of Platinum Drugs from HoIG-Pt.

HoIG-Pt (30 mg) were dispersed in simulated body fluid (SBF, pH 7.3) (50 mL) and kept at 37° C. with stirring at 600 rpm. An aliquot (3 mL) was withdrawn after centrifugation of the suspension at each specified time period and was replaced with equal volume of fresh SBF. The concentrations of the released Pt drugs were measured using a UV/Vis spectrometer.

Neutron activation of HoIG, HoIG-Pt. Dry ¹⁶⁶HoIG and ¹⁶⁶HoIG-Pt were neutron-activated in a 1 MW TRIGA Mark I nuclear reactor at the Texas A&M Nuclear Science Center in a thermal neutron flux of approximately 7×10¹² neutrons/cm²·s for >0.2 h. Gamma radioactivity was measured before shipment to UNTHSC and again directly prior to performing cell studies using a calibrated WIZARD2 Automatic Gamma Counter (PerkinElmer).

Cytotoxicity Studies.

The studies involving human NSCLC A549 cells was carried out under standard conditions in a humidified, 37° C., 5% CO₂ atmosphere, incubator. The culture medium used for A549 was Roswell Park Memorial Institute with 10% fetal calf serum (FCS), 100 μg/mL streptomycin, 100 IU/mL penicillin and 2.0 mM L-glutamine (RPMI).

Suspensions of each type of neutron-activated nanoparticle were prepared in RPMI. Two control groups, RPMI alone and RPMI with cells not exposed to ¹⁶⁶Ho nanoparticles were included in each 96-well plate. At least four replicates were done for each concentration and each control group. The cells were seeded at 5×10⁴ cells/mL (100 μL/well) in 96-well plates and allowed to grow for 24 h after which time the RPMI was removed and replaced with 100 μL of RPMI that contained blank ¹⁶⁶HoIG or ¹⁶⁶HoIG-Pt. After an exposure time of 24 h on a microplate shaker in the incubator, the RPMI was removed and replaced with 100 μL of fresh RPMI. To each well, 20 μL of CellTiter 96® AQueous One solution cell proliferation (MTS) assay solution was added. After 1 h incubation with the MTS solution, the absorbance was read at 490 nm using a Synergy™ H1 hybrid multi-mode microplate reader. The percent survival of cells treated by each concentration of nanoparticles was calculated using the following equation:

$\begin{matrix} {{\% \mspace{14mu} {survival}} = {100 \times \left\lbrack \frac{A_{d} - A_{m}}{A_{c} - A_{m}} \right\rbrack}} & (1) \end{matrix}$

where A_(d) is the absorbance of cells treated with nanoparticles, A_(m) is the absorbance of medium alone and A_(c) is the absorbance of cells without treatment. The % survival data was fit to exponential regressions using Excel Solver, and IC₅₀ values calculated.

Cytotoxicity studies involving free cisplatin, carboplatin and oxaliplatin were done in the same manner. The only difference was that the microplate shaker was not used, as all three drugs can be dissolved in RPMI.

Animal Studies.

Cells and Animals.

A549 human lung adenocarcinoma cells were obtained from American Type Culture Collection (ATCC). Female T cell-deficient athymic nude mice were obtained from Harlan Laboratories. All animal procedures were performed following a protocol approved by the University of North Texas Health Science Center Institutional Animal Care and Use Committee in accordance with the NIH Guidelines.

Subcutaneous A549 xenograft model.

A549 human lung adenocarcinoma cells (5×10⁶) resuspended in a total volume of 100 μL of PBS and Matrigel (1:1) were injected into the flank of the left hind leg of each mouse. Tumor volumes were monitored twice a week by measuring two perpendicular diameters with calipers. Tumor volume (V) was calculated using the following equation:

V=(L×W ²)/2  (2)

where L is the length (large diameter), and W is the width of the tumor (small diameter), both in millimeters. Each magnet used in this study was 2.5 g and 12,000 Gauss; it was placed on the top of the tumor and kept in place using Nexcare Steri-strip skin adhesive surgical tape strips. HoIG-cisplatin and ¹⁶⁶HoIG-cisplatin suspensions were prepared using phosphate-buffered saline (PBS) containing 10% of polyethylene glycol 1500 (PEG1500). The dose of cisplatin incorporated in HoIG or ¹⁶⁶HoIG, which was injected into to each mouse, was 5 mg/kg.

Ratio of Percent Weight Metal in Tumor to Liver after i.v. Injection of HoIG-Cisplatin.

Five million A549 cells were injected subcutaneously into the flank of the left hind leg of each mouse and when tumor size was approximately 50 mm³, mice were randomized into two groups (n=4 each). To the first group, a magnet was taped on the top of the tumor as described earlier and 100 μL of HoIG-cisplatin suspension was injected via tail vein; mice were exposed to magnets during and 5 h after injection of HoIG-cisplatin. The second group received the same injection at the same time without an attached magnet. Both groups were sacrificed immediately after the 5 h duration and tumors and livers harvested and digested using 70% nitric acid at 70° C. The Pt and Ho contents in tumor and liver samples were characterized using ICP-MS.

Efficacy Study.

To female athymic nude mice, 5 million A549 cells were injected subcutaneously into the flank of the left hind leg of each and when tumor size was approximately 50-100 mm³, mice were randomized into groups (n>6 per group each). Magnets were applied to Group 1-3 but not Group 4. To Group 1 and 2, a magnet was taped on top of the tumor and injected with 100 μL of radioactive ¹⁶⁶HoIG-cisplatin (Group 1) or HoIG-cisplatin (Group 2) suspension through tail vein; mice were exposed to magnets during and 5 h after injection. To Group 3, a magnet was taped in the same manner but without nanoparticle injection; mice were exposed to magnets for 5 h. Group 4 was a control group without magnet or injection. Tumor growth was monitored once every five days for up to 35 days.

Nanoparticle Characterization.

The x-ray diffraction patterns were collected on a Rigaku Ultima IV x-ray diffractometer using Cu Kα radiation. The morphology of the synthesized HoIG was analyzed using transmission electron microscopy (TEM). TEM analysis was performed on a JEOL 2100 analytical TEM with an accelerating voltage of 200 kV. EDX analysis of carbon coated samples were carried out using a Zeiss-LEO model 1530 SEM. The magnetic properties of the nanoparticles was measured using a superconducting quantum interference device (MPMS-XL from Quantum Design), and the saturation magnetization (M_(s)), remnance (M_(r)) and coercivity (H_(c)) were determined from the hysteresis loops. Magnetic susceptibility (χ_(N)) and relative permeability (μ_(r)) were calculated from the linear slope of the M(H) curve. The zetapotential measurements of nanoparticles were determined using Malvern Zetasizer Nano ZS.

Results and Discussion

Holmium Iron Garnet Nanoparticles (HoIG).

HoIG was synthesized using a hydroxide co-precipitation method. FIGS. 27 a and 27 b show the PXRD pattern for the as synthesized HoIG samples. The phase matches well with Fe₅Ho₃O₁₂ (JCPDS 00-023-0282). The crystal size was calculated from the PXRD line broadening of the (420) peak using the Scherrer equation, D_(hkl)=kλ/B cos θ, where D_(hkl) is the particle size in nm, k is a constant (shape factor) with a value of 0.9, B is the width of half maximum, and λ is the wavelength of the x rays. The D_(hkl) value of HoIG was approximately 52 nm.

The TEM image of synthesized HoIG (FIG. 28 a) exhibits a rounded irregular shape. The average size of the nanoparticles is 40.7±16.4 nm in length and 26.9±8.0 nm in width. The interplanar distance of HoIG in FIG. 28 b is 0.28 nm, which corresponds to the (420) plane d=0.27670 nm in FIGS. 27 a and 27 b. These results indicate that nanocrystalline HoIG powder was successfully prepared by the hydroxide co-precipitation method. The synthesized HoIG is olive green in color and show magnetic properties. The magnetization of the synthesized HoIG powder was performed at room temperature. The plot of magnetization (M) (normalized to the mass of magnetic material) as a function of magnetic field (H) is shown in FIG. 29.

The saturation magnetization (M_(s)) is defined as the state at which an increase in the magnetic field does not lead to further increase in the magnetization of the material. M_(s), reached 8.9 emu/g with the average particle size of 50 nm. The coercive field (H_(e), the external magnetic field required to bring the magnetization to zero) was 50 Oe. The reported saturation magnetization of YIG particles with an average 25 nm size was 20.6 emu/g and the coercivity is 51 Oe (Rajendran et al., 2006). The principal magnetic interaction in HoIG is the superexchange in the (Fe³⁺)_(A)—O²—(Fe³⁺)_(D) triads. This interaction forms two antiparallel iron sublattices with the easy axis along the (111) direction. The rare earth moments are antiparallel to the iron spins owing to the (C-D) exchange interaction (Lataifeh et al., 2000). In the case of YIG there is no magnetic contribution from Y³⁺ due to the closed shell yttrium ions. But there is a magnetic contribution from Ho³⁺ ions antiparallel to the iron spin in HoIG which results in low saturate magnetization for HoIG as compared to the YIG nanoparticles. The remnant magnetization (M_(r)) was 2.8 emu/g for HoIG. The calculated magnetic susceptibility (χ_(m)) using the linear part of the magnetization slope (Nguyet et al., 2013) was 2.08 and relative permeability (μ_(r)=1+χ_(m)) was 3.08. These results are consistent with the room temperature soft ferromagnetic behavior of these materials (Rajendran et al., 2006).

Platinum Drug Loaded HoIG Nanoparticles (HoIG-Pt).

The FTIR spectrum showed the successful loading of platinum drugs in to HoIG. The ATR-FTIR spectrum of cisplatin showed the characteristic amine stretching in the range 3400-3200 cm⁻¹, the asymmetric amine bending in the range 1600-1500 cm⁻¹ and the symmetric amine bending in the range 1300-1200 cm⁻¹ (Yan et al., 2005). The characteristic asymmetric amine stretching in the range 3145-3268 cm⁻¹ of carboplatin was also observed (Wysoninski et al., 2006) as was the characteristic asymmetric amine stretching band in the range of 3346-3460 cm⁻¹, the degenerate deformation vibration of amino group at 1610 cm⁻¹ and wagging mode of the amino group at 1609 and 1620 cm⁻¹ for oxaliplatin (Tyagi et al., 2008). It has been reported that when the oxide materials are dehydroxylated by increasing the temperature that there is an increase in ammonia hydrogen bonding to the oxygen atoms of the material (Pugh et al., 1994). Therefore, annealed HoIG at high temperature shows no characteristic hydroxyl stretching in the FTIR. Thus, the surface of HoIG is dehydroxylated and there is a tendency for binding of amine groups of platinum drugs to the oxygen atoms of the HoIG through hydrogen bonding. The red shift of the characteristic amine stretching and bending bands of cisplatin, carboplatin and oxaliplatin are ascribed to the hydrogen bonding of platinum drug molecules with surface oxide groups of the HoIG (FIG. 30). Energy-dispersive x-ray spectroscopy (EDX) further confirmed the presence of the platinum drugs on HoIG.

The weight percent of Ho and Pt, determined using ICP-MS are shown in Table 6.

TABLE 6 Weight percentage of Ho and Pt in HoIG and HoIG-Pt derivatives Sample Wt % Pt Wt % Ho HoIG — 55.6 HoIG-cisplatin¹ 6.2 47.1 HoIG-carboplatin 3.2 51.2 HoIG-oxaliplatin 2.2 52.9 ¹HoIG-cisplatin Pt ± 3.5 and Ho ± 6.1.

The stability of HoIG-Pt at different pH values is shown in FIG. 31. The isoelectric point of HoIG is 3.7, and the isoelectric point of cisplatin, carboplatin and oxaliplatin loaded HoIG are 3.9, 4.0 and 4.9, respectively. When the pH value of the solution is less than the isoelectronic point, the HoIG and HoIG-Pt are positively charged, and they are negatively charged when the pH is above the isoelectronic point. The zeta potential of HoIG in neutral aqueous media was determined to be −35.4 mV. This negative potential is due to the negatively charged oxide surface of HoIG. However the zetapotential of platinum drug loaded HoIG was higher than that of HoIG. The zetapotential of HoIG-cisplatin, HoIG-carboplatin and HoIG-oxaliplatin was −28.1, −20.2 and −26.7, respectively. This may reflect a decrease in negative surface charge of HoIG after the platinum drug was conjugated with the HoIG. It has been reported that cisplatin loaded poly(acrylic acid-co-methyl methacrylate) (p(AA-MMA)) microparticles are less electronegative (˜−40 mV) than the blank (p(AA-MMA)) microparticles (˜−42 mV) (Yan et al., 2005a). Cisplatin conjugated calcium phosphate nanoparticles (CaPNPs) are also less electronegative (−27.9 mV) than that of blank CaPNPs (−45.59 mV) (Cheng et al., 2007). Cisplatin-, carboplatin- and oxaliplatin-loaded HoIG are approximately −30 mV, −23 mV and −26 mV, respectively, at pH 7.35-7.45, which is a predictor for stability in the blood. It has been reported that superparamagnetic nanoparticles showed a zetapotential of −18.3 mV at physiological pH 7.2, and had a high stability in vitro (Sun et al., 2009).

In Vitro Release of Platinum Drugs from HoIG-Pt.

The amount of Pt released from the nanoparticles over time was measured by UV/Vis spectroscopy. The controlled release of platinum drugs from the nanoparticles is shown in FIGS. 32 a-32 c. 80% of cisplatin, carboplatin and 60% of oxaliplatin were released after 1 h (FIGS. 32 a-32 c). Thereafter, a period of controlled platinum release occurred, reaching a value of 99% after 400, 250 and 500 min, for HoIG-cisplatin, HoIG-carboplatin and HoIG-oxaliplatin, respectively.

To further analyze the in vitro release data, various kinetic models were used to describe the release kinetics. The zero order rate describes the systems where the drug release rate is independent of its concentration. A first order describes the release from system where the release rate is concentration dependent. Higuchi describes the release of drugs from an insoluble matrix as a square root of time dependent process based on Fickian diffusion. The Hixson-Crowell cube root law describes the release from systems where there is a change in surface area and diameter of particles or tablets (Munaweera et al., 2004a; Dash et al., 2010).

The linear plots of, cumulative % drug release vs. time (zero order kinetic model), log cumulative of % drug remaining vs. time (first order kinetic model), cumulative % drug release vs. square root of time (Higuchi model), log cumulative % drug release vs. log time (Korsmeyer-Peppas model), and cube root of drug % remaining in matrix vs. time (Hixson-Crowell model) (Munaweera et al., 2014a) were plotted and compared.

TABLE 7 R² values of linear plots of different kinetic models for drug release from Pt-HoIG HoIG- HoIG- HoIG- Kinetic model cisplatin carboplatin oxaliplatin Zero order 0.800 0.837 0.960 First order 0.988 0.981 0.985 Higuchi 0.912 0.927 0.983 Korsmeyer-Peppas 0.970 0.966 0.973 Hixson-Crowell 0.944 0.964 0.962

Table 7 shows the R² values of linear plots of different kinetic models for platinum drugs release from HoIG-Pt. According to the R² values the best linearity can be found in first order model (R²=0.988, 0.981 and 0.985) indicating the release rate is concentration dependent.

Neutron-Activation of HoIG and HoIG-Pt.

Dry HoIG and HoIG-Pt were neutron-activated in a 1 MW TRIGA Mark I nuclear reactor at the Texas A&M Nuclear Science Center. When HoIG was neutron-activated in a thermal neutron flux of approximately 7×10¹² neutrons cm⁻² s⁻¹ for 0.45 h, the radioactivity directly afterwards was approximately 250 μCi mg⁻¹. By quantifying the 81 keV photons emitted, the ¹⁶⁶HoIG prepared here has a ¹⁶⁶Ho content of approximately 49% w/w, which corroborates our ICP-MS data.

Ho-incorporated mesoporous silica nanoparticles, ¹⁶⁶Ho-MSNs (size 80-100 nm), with a radioactivity of 327 μCi mg⁻¹ after 2.2 h neutron-activation in a thermal neutron flux of 5.5×10¹² neutron cm⁻² s⁻¹, and ¹⁶⁶Ho-incorporated mesoporous silica MCM-41 nanoparticles, ¹⁶⁶Ho-MCM-41 (size 400 nm), with a radioactivity of 150 μCi mg⁻¹ after 2 h neutron-activation in the same thermal neutron flux, were previously prepared (Di Pasqua et al., 2013; Di Pasqua et al., 2012). Holmium acetylacetonate nanoparticles (78 nm) prepared for radioablation of solid malignancies resulted in 324 μCi mg⁻¹ after 1 h neutron-activation in a thermal neutron flux of 5×10¹² neutron cm⁻²s¹ (Bult et al., 2010). Also, polylactic acid (PLA) microspheres with an average diameter of 37 μm and labeled with ¹⁶⁶Ho for internal radionuclide therapy of liver metastases were 1351 μCi mg⁻¹ after 1 h exposure to a neutron flux of 5×10¹³ neutrons cm⁻² s⁻¹ (Nijsen et al., 1999).

Cytotoxicity Studies of HoIG and HoIG-Pt.

Human NSCLC A549 cells were treated with blank ¹⁶⁶HoIG, free-cisplatin, -carboplatin, -oxaliplatin, ¹⁶⁶HoIG-cisplatin, ¹⁶⁶HoIG-carboplatin or ¹⁶⁶HoIG-oxaliplatin, FIG. 33, for 24 h at 37° C. As is shown in FIG. 33 a, at the radioactivities used, the blank magnetic nanoparticle formulation, ¹⁶⁶HoIG, was only slightly toxic toward NSCLC A549 cells. The studies involving the Pt drug-loaded nanoparticles, ¹⁶⁶HoIG-cisplatin, ¹⁶⁶HoIG-carboplatin and ¹⁶⁶HoIG-oxaliplatin, were performed using approximately the same Pt to radiation ratio (˜80 μM/μCi). ¹⁶⁶HoIG-cisplatin and ¹⁶⁶HoIG-oxaliplatin, exhibited much higher levels of toxicity toward A549 cells, FIG. 33 d and e, than ¹⁶⁶HoIG and free cisplatin and oxaliplatin, FIGS. 33 b and c, respectively. Free carboplatin, however, did not act synergistically with radiation (data now shown). To further investigate its cytotoxicity in vitro, another ¹⁶⁶HoIG-cisplatin study was performed, this time with a higher ratio of Pt to radiation (˜230 μM/μCi, FIG. 34). This study confirmed that low amounts of radiation act synergistically with cisplatin.

Platinum-derived drugs have been used as radiosensitizers (Geldof et al, 1996). Preclinical studies have shown that the combination of the drug with radiation increases toxicity toward tumor cells, but the mechanism remains unclear (Rezaee et al., 2013). It was reported that the yield of DNA strand breaks increased during radiotherapy when cisplatin was present (Rezaee et al., 2013). A distinct advantage of the present system is that the Pt-based chemotherapeutic and ¹⁶⁶Ho can be delivered together via a magnetic field and act synergistically.

Animal Studies.

Distribution of HoIG-cisplatin in tumors and livers was investigated using a subcutaneous NSCLC A549 xenograft athymic nude mouse model. Five million A549 cells were injected subcutaneously to each mouse; when tumor size reached approximately 50 mm³, one group of mice were exposed to an external magnetic field and received HoIG-cisplatin injection via tail vein injection, while the other group received the same injection without exposure to an external magnetic field. After the first group had been exposed to a magnetic field for 5 h, tumor and liver tissues of both groups were harvested. Using ICP-MS, Pt and Ho contents in tumor and liver samples were measured. As illustrated in FIG. 35, for Pt, the ratio of metal contents in tumor to liver was 1.84±0.46 with magnet and 1.06±0.17 without an magnet; for Ho, the values were 0.29±0.08 with magnet and 0.03±0.01 without magnet. In both cases, the differences were significant (p<0.05). This indicates that when an external magnetic field is applied, HoIG-cisplatin localizes in tumors, more so than when no magnet is applied, which suggests that magnetic targeting was achieved using this system.

In the efficacy study, the same magnetic targeting system was used. Five million NSCLC A549 cells were injected subcutaneously in each mouse; when tumor volumes reached approximately 50-100 mm³, Groups 1-3, which are blue, green and light red, respectively in FIG. 36, were exposed to an external magnetic field and received radioactive ¹⁶⁶HoIG-cisplatin, non-radioactive HoIG-cisplatin and no treatment, respectively. A control group, Group 4, which is grey in FIG. 36, was given no treatment and was not exposed to a magnet. Magnets applied in Groups 1-3 were removed after 5 h exposure and tumor growth monitored once every five days for 35 days after treatment. Tumor volumes were measured and tumor volume ratios calculated using tumor volume on the day of measurement divided by tumor volume on the day of treatment (Day 0). As is shown in FIG. 36, after 35 days, the tumor volume ratio for Group 3 and that for Group 4, were very similar, which indicates that the applied external magnetic field by itself has no impact on tumor growth.

Thirty-five days after radioactive ¹⁶⁶HoIG-cisplatin injection, the tumor volume ratio of Group 1 was significantly lower than that of Group 3 and of Group 4, with p<0.05 in both cases, demonstrating the inhibition of tumor growth by this chemoradiotherapeutic magnetic nanoparticle compared to no treatment controls. Group 2, treatment with HoIG cisplatin, was lower than no treatment controls, but not significantly; thus, radiation (200 μCi per mouse) contributed to the tumor growth inhibition.

Example 7

Here we describe a new and improved strategy for the radiotherapeutic treatment of squamous cell carcinoma (SCC). ¹⁶⁵Ho-containing nanoparticles and NO-releasing nanozeolites will be homogeneously incorporated into electrospun polymer nanofibrous mats; after being made radioactive via neutron-activation, the bandage will conform to the cancer site and treat the covered area. The β⁻ energy of ¹⁶⁶Ho will be sufficient to damage DNA in cancer cells just beneath the outermost layer of the epidermis, and the bandage will store and release NO, a radiosensitizer that will allow for lower doses of radiation to be used. Because radiation can be both beneficial, in regards to treatment, and detrimental, in regards to healthy tissues, lower doses with the same efficacy as higher doses are preferable. Unlike a tumor lesion, the surrounding healthy skin has a stratum corneum, which will offer protection from low doses of radiation. This combination should help patients achieve optimized cosmetic and/or functional outcomes without the use of cumbersome equipment and specialized instrumentation and facilities.

The “radiotherapeutic bandage” described herein comprises a radiotherapeutic nuclide, i.e., ¹⁶⁶Ho, as well as a nanozeolite that releases NO, a radiosensitizer that will allow for lower doses of radiation to be used in therapy. The bandage can be prepared via electrospinning, a simple approach that uses electrostatic forces to produce nanofibrous materials and allows for nanoparticles to be homogenously distributed throughout. The thickness of these materials can be varied by controlling parameters such as spinning duration, polymer concentration, applied voltage, temperature and humidity. The electrospinning method is attractive because of its low cost and suitability for mass production. Furthermore, after being incorporated, nanoparticles are not released during application. The bandage is also easily manipulatable to fit the specific size and location of the tumor lesion.

Methods:

1) Prepare stable electrospun polymer nanofibrous mats containing ¹⁶⁶Ho-nanoparticles and NO-releasing nanozeolites. A hydroxide co-precipitation method will be used to prepare the ¹⁶⁵Ho-nanoparticles (¹⁶⁵HoIG). ¹⁶⁵Ho nitrate will be stirred in ethylene glycol and 6 M sodium hydroxide used to precipitate ¹⁶⁵Ho-nanoparticles; these nanoparticles will then be annealed at 900° C. for 3 h to obtain a crystalline product. The nanozeolites can be prepared as follows. Aluminum isopropoxide, trimethylammonium hydroxide, 1 M sodium hydroxide solution and water will be stirred at 40° C. until clear. Separately, 30% silica sol will be combined with water and stirred at 40° C. until clear. These will then be combined and placed in an oven for 24 h at 80° C., and the resulting nanozeolites washed, collected and dried. Both of these nanomaterials will be characterized with dynamic light scattering (DLS), X-ray diffraction (XRD) spectroscopy and transmission electron microscopy (TEM), and the ¹⁶⁵Ho content of the nanoparticles determined using inductively coupled plasma-mass spectrometry (ICP-MS). The ¹⁶⁵Ho-nanoparticles and nanozeolites will be incorporated into a nanofibrous mat via electrospinning Briefly, the nanomaterials will be dispersed in dimethylformamide (DMF) at room temperature, as will polyacrylonitrile (PAN), separately. The two solutions will then be mixed with continuous stirring until a homogeneous suspension is obtained, which will then be passed through a syringe with a spinneret needle using a syringe pump and a voltage of approximately 13 kV applied to the needle. The nanozeolites in the blend will be made to adsorb NO by induction of NO in a purged heated oven. Modulation of the rate and extent of NO release can be easily accomplished by modifying the nanozeolites and the fiber porosity of the mat. Neutron-activation in a thermal neutron flux of approximately 3.5×10¹² n/cm²·s in a 1 MW nuclear reactor will produce ¹⁶⁶Ho-nanoparticles in the mat. After production of this “radiotherapeutic bandage”, its radioactivity will be determined by quantifying the photons emitted using a PerkinElmer γ spectrometer and release of NO assessed with Griess reagent and UV-visible spectroscopy. Its overall stability after various neutron-activation times will be determined by visual inspection and scanning electron microscopy (SEM).

Polymer blends containing ¹⁶⁶Ho-nanoparticles and NO-releasing nanozeolites will be evaluated in SCC cell lines, i.e., SRB-1, SRB-12, Colo-16 and UT-SCC-14, and an optimized ratio of ¹⁶⁶Ho radioactivity to NO concentration in the mat will be determined for use in the final blend of the “radiotherapeutic bandage”. Cells will be maintained in DMEM growth medium with 10% fetal bovine serum and 1% penicillin/streptomycin, and grown in a 37° C., 5% CO₂ incubator. Mats with various ratios of ¹⁶⁶Ho radioactivity to NO concentration will be placed in culture medium over monolayers of SCC cells for 24 h and apoptosis determined using an Annexin V FITC assay. Percent cell apoptosis will be used as the measure of a therapy's efficacy. No nanoparticles are expected to be released from the mat when immersed in solution and controls, including non-radioactive bandages with no NO, will be tested to rule out any effect of the polymers; thus, only the effects of radiation and NO from the intact bandage will be studied. Prior to the aforementioned cell studies, the release profile of NO from the mats will be determined using the Griess reagent and UV-visible spectroscopy, so the concentrations of NO that cells are exposed to over the 24 h period can be determined. Animal studies will also be performed following a protocol approved by the University of North Texas Health Science Center Institutional Animal Care and Use Committee (IACUC) in accordance with the NIH Guidelines. Based on its sensitivity to the ¹⁶⁶Ho/NO combination therapy, a human SCC cell line from Aim 2 will be selected; approximately 4 week old female athymic nude mice will be used and five million cells injected subcutaneously into the left hind-leg of each. When tumors are approximately 50 mm³ in diameter, the optimized “radiotherapeutic bandage” and controls will be applied with Nexcare Steri-Strip surgical tape for 24 h. The following groups will be studied: 1) No treatment, 2) Non-radioactive bandage with no NO, 3) NO-releasing non-radioactive bandage, 4)¹⁶⁶Ho-containing bandage with no NO, and 5) NO-releasing ¹⁶⁶Ho-containing bandage, i.e., “radiotherapeutic bandage”. NO is capable of diffusing through the skin and the 13 energy of ¹⁶⁶Ho is sufficient to penetrate the xenograft; thus, this animal model is appropriate for the study of our “radiotherapeutic bandage”. Before and then three times a week after treatment, tumor sizes will be measured using a caliper; this will be done for 30 days post-therapy, which is sufficient to observe the inhibition of tumor growth after a one time treatment, and inhibition of tumor growth will be compared among all five groups to determine efficacy. Mice will then be sacrificed for pathologic evaluations to determine if any damage to muscles or internal organs resulted from therapy, and to compare damage, if any, between groups.

An electrospun polymer nanofibrous mat containing ¹⁶⁵Ho-nanoparticles has been made and remains completely intact after neutron-activation. Furthermore, ¹⁶⁶Ho is homogenously distributed throughout the mat, which is critical for efficient radiotherapy. We have also prepared a prototype “radiotherapeutic bandage” that contains ¹⁶⁵Ho and releases NO.

Example 8 Materials

Holmium (III) nitrate hexahydrate, sodium hydroxide, ethylene glycol, polyacrylonitrile (Molecular weight: 150,000 mol/g) were purchased from the Aldrich Chemical Co. Iron (III) nitrate hexahydrate was purchased from Acros Organics. Dimethylformamide (DMF) was purchased from Fisher Scientific. All reagents were used as received.

Synthesis of HoIG Nanoparticles.

¹⁶⁵HoIG nanoparticles were synthesized by modifying a reported procedure (Munaweera et al., 2014). Stoichiometric mixtures (5:3) of 1 M iron(III) nitrate (5 mL) and 1 M holmium(III) nitrate (3 mL) were mixed with ethylene glycol (21 mL) at room temperature with stirring. Then 6 M NaOH (10 mL) was added drop wise to form the ¹⁶⁵HoIG nanoparticle precipitate. The product was centrifuged and washed with de-ionized water, then dried at 100° C. overnight. The ¹⁶⁵HoIG was annealed in air at 900° C. for 3 h.

Electrospinning of Polyacrylonitrile Polymer Solutions with ¹⁶⁵HoIG Nanoparticles (¹⁶⁵HoIG/PAN).

Polyacrylonitrile (PAN) (1.0 g) was dispersed in dimethylformamide (DMF) (5 mL), with gentle heating and stirring. ¹⁶⁵HoIG nanoparticles were dispersed in DMF (5 mL) and mixed with the PAN solution at room temperature to prepare 33 and 50% w/w dispersions (Table 8). The PAN solutions containing ¹⁶⁵HoIG nanoparticles were drawn into a 12 mL syringe equipped with a 20 gauge needle and electrospun on an aluminum foil substrate wrapped around a rotating drum. The electro spinning conditions are listed in the Table 8.

TABLE 8 ¹⁶⁵HoIG Volume Electrode nano- of separation PAN particles DMF Rate Voltage distance Sample (g) (g) (mL) (mL/h) (kV) (cm) 33% (w/w) 1.0 0.5 10 0.05 14 6 ¹⁶⁵HoIG 50% (w/w) 1.0 1.0 10 0.05 14 6 ¹⁶⁵HoIG

Neutron Activation of ¹⁶⁵HoIG and ¹⁶⁵HoIG/PAN.

¹⁶⁵HoIG nanoparticles (5 mg) and approximately 0.5×0.5 cm² (6 mg)¹⁶⁵Ho-containing polymer nanofibrous mats cut from both the 33% (w/w) and 50% (w/w)¹⁶⁵HoIG/PAN were neutron-activated in a 1 MW TRIGA Mark I nuclear reactor at the Texas A&M Nuclear Science Center in a thermal neutron flux of approximately 3.5×10¹² neutrons/cm²·s for 0.5, 1.0, 2.0 or 4.0 h. Radioactivities were determined by quantifying the photons emitted using a gamma spectrometer. The radioactivities directly after neutron-activation are reported.

Characterization.

X-ray diffraction patterns were collected on a Rigaku Ultima IV x-ray diffractometer using Cu Kα radiation. The morphology of the synthesized ¹⁶⁵HoIG nanoparticles and electrospun fibers were analyzed using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). SEM analysis of Au/Pd coated samples were carried out using a Zeiss-LEO model 1530 SEM. TEM analysis was performed on JEOL 2100 analytical TEM with an accelerating voltage of 200 kV. Fourier Transform Infrared Spectroscopy (FTIR) analysis of ¹⁶⁵HoIG nanoparticles and bandages were carried out using a Nicolet 380 spectrometer equipped with an Attenuated Total Reflectance (ATR) attachment. TGA analysis was performed using TA Instruments SDT Q600. Inductively coupled plasma-mass spectrometry (ICP-MS) was performed to determine the ¹⁶⁵Ho content in ¹⁶⁵HoIG using NexION 300D from PerkinElmer. Gamma radiation of neutron activated samples was measured using Canberra Industries HPGe GC3518.

¹⁶⁵HoIG Nanoparticles.

FIGS. 27A and B shows the PXRD patterns for the as synthesized ¹⁶⁵HoIG nanoparticles. The phase matches well with Fe₅Ho₃O₁₂ (JCPDS 00-023-0282). The crystallite sizes were calculated from the PXRD line broadening of the 420 reflection using the Scherrer equation, D_(hkl)=kλ/B cos θ, where D_(hkl) is the particle size in nm, k is a constant (shape factor) with a value of 0.9, B is the width of half maximum, and λ is the wavelength of the x rays. The D_(hkl) value of ¹⁶⁵HoIG is about 52 nm.

TEM images of the as synthesized ¹⁶⁵HoIG nanoparticles are shown in FIGS. 28A and B. The nanoparticles generally exhibited a rounded irregular shaped morphology. The length of ¹⁶⁵HoIG is 55 nm and the width is 28 nm. The interplanar distance of ¹⁶⁵HoIG is 0.28 nm (FIG. 28 (b) which corresponds to the (420) plane is d=0.278 nm in FIG. 27. Using ICP-MS, the ¹⁶⁵HoIG was determined to contain 55.6% (w/w) Holmium.

Electrospinning of PAN Containing HoIG Nanoparticles.

SEM images of the electrospun fiber mats with different ¹⁶⁵HoIG nanoparticle loadings are shown in FIGS. 23A and B. As shown in the histogram 90% of fibers are below 300 nm. The average diameter of nanofibers are 174±56 nm and 208±54 nm when the ¹⁶⁵HoIG loading were 33% and 50% (w/w). The increase in the fiber diameter with increasing ¹⁶⁵HoIG content may reflect the size of the garnet nanoparticles as well as agglomeration (Munaweera et al., 2014; Hassan et al., 2014).

Radiotherapeutic bandages (before and after neutron activation) were soaked in simulated body fluid (SBF) and DI water for 4 and 8 h and samples from SBF and water were analyzed using TEM to check whether there is any loss of the embedded nanoparticles from the PAN fibers. There were no free nanoparticles detected in the samples. These results confirm that radioactive particles do not leach out from the radiotherapeutic bandage.

Neutron-Activation of ¹⁶⁵HoIG Nanoparticles and ¹⁶⁵HoIG/PAN Bandages.

¹⁶⁵HoIG and rectangles of ¹⁶⁵HoIG/PAN were neutron-activated for 0.5, 1, 2 and 4 h. Radioactivities of 56.8, 330.7, 833.8 and 1633.6 μCi/mg were obtained for ¹⁶⁶HoIG nanoparticles, after approximately 0.5, 1, 2 and 4 h neutron-activation, respectively. From these data, we can calculate that ¹⁶⁶HoIG nanoparticles contain 57.8±26.2% (w/w) ¹⁶⁶HoIG which corroborates the ICP-MS data.

It is critical for the ¹⁶⁶HoIG/PAN bandage to emit radiation uniformly during therapy; thus, four rectangular pieces were cut from a 33% ¹⁶⁵HoIG/PAN in four different locations and neutron-activated for 0.5 h. The same was done for the 50% HoIG/PAN bandage. After neutron-activation, the radioactivities were measured and ¹⁶⁶Ho content determined; 17.1±0.7% and 22.7±1.9% of ¹⁶⁶Ho was contained in electrospun fibers with 33% (w/w) HoIG and 50% (w/w) HoIG, respectively. This is consistent with a uniform dispersion of ¹⁶⁶HoIG throughout the bandage after electrospinning, as well as efficient loading of HoIG into the bandage.

Radioactivities of 48.1, 101.1, 479.2 and 650.3 μCi/mg were produced for 33% HoIG/PAN, and 63.7, 163.3, 300.0 and 854.7 μCi/mg for 50% HoIG/PAN, after 0.5, 1, 2 and 4 h neutron-activation, respectively. Thus, radioactivities of 6.420×10², 1.675×10³, 1.917×10⁴ and 2.016×10⁴ μCi/cm² were produced for 33% HoIG/PAN bandages, and 1.411×10³, 6.532×10³, 4.501×10³ and 2.607×10⁴ μCi/cm² were produced for 50% HoIG/PAN bandages.

Radioactivity can be calculated using the following formula:

A=nfs(1−e ^(−λT))e ^(−λt),

where A is radioactivity produced (Bq/mg, which is 2.7×10⁻¹¹ Ci/mg), n is number of atoms per mg, f is neutron flux density (n/cm²·s), s is thermal neutron capture cross section (cm²), λ is decay constant (0.693/t_(1/2)), T is irradiation time and t is decay time. Here, nfs is a constant, and immediately after neutron-activation, t is 0. Thus, A should be proportional to 1−e^(−λT). We here plot radioactivity (A) in μCi/mg against 1−e^(−λT) (FIG. 16F). Least-squares linear fits give R² values of 0.93 0.96 and 0.98 for the 33 and 50% HoIG/PAN and HoIG data sets, respectively.

This example demonstrates ¹⁶⁶Ho containing bandages with different amounts of radioactivity can be prepared by varying the neutron-activation time and the amount of neutron-activatable nuclide incorporated. Preparing and handling large amounts of hazardous, highly radioactive materials with short half-lives can be cumbersome and, thus, is here avoided using neutron-activatable ¹⁶⁵Ho. The β⁻ energy of ¹⁶⁶Ho should be sufficient to damage DNA in cancer cells just beneath the outermost layer of the epidermis, and it is expected that the stratum corneum will protect any normal skin surrounding the tumor lesion from radiation damage. Thus, this approach could help patients achieve optimized cosmetic and/or functional outcomes without the use of specialized instrumentation or facilities. It is envisioned that a lead wrap could be placed around the bandage during treatment while sitting in a physician's office.

REFERENCES

-   Munaweera, I.; Aliev, A.; Balkus, K. J. “Electrospun Cellulose     Acetate-Garnet Nanocomposite Magnetic Fibers for Bioseparations” ACS     Appl. Mater. Interfaces 2014, 6, 244. -   Rajendran, M.; Deka, S.; Joy, P. A.; Bhattacharya, A. K. J. Magn.     Magn. Mater. 2006, 301, 212. -   Lataifeh, M. S. J. Phys. Soc. Jpn. 2000, 69, 2280. -   Nguyet, D. T. T.; Duong, N. P.; Satoh, T.; Anh, L. N.;     Hien, T. D. J. Magn. Magn. Mater. 2013, 332, 180. -   Yan, X.; Gemeinhart, R. A. J. Controlled Release 2005, 106, 198. -   Wysokiński, R.; Kuduk-Jaworska, J.; Michalska, D. J. Mol. Struct.:     THEOCHEM 2006, 758, 169. -   Tyagi, P.; Gahlot, P.; Kakkar, R. Polyhedron 2008, 27, 3567. -   Pugh, R. J. and Bergstrom, L., Surface and Colloid Chemistry in     Advanced Ceramic Processing, Surfactant Science Series; Marcel     Dekker: New York, 1994. -   Yan, X.; Gemeinhart, R. A. J. Controlled Release 2005a, 106, 198. -   Cheng, X.; Kuhn, L. Int. J. Nanomed. 2007, 2, 667. -   Sun, H.-W.; Zhang, L.-Y.; Zhu, X.-J.; Wang, X.-F. J. Biomater. Sci.,     Polym. Ed. 2009, 20, 1675. -   Munaweera, I.; Koneru, B.; Shi, Y.; Di Pasqua, A. J.; Balkus,     Jr. K. J. APL Mater. 2014a, 2, 113315. -   Dash, S.; Murthy, P. N.; Nath, L.; Chowdhury, P. Acta Pol. Pharm.     Drug Res. 2010, 67, 217. -   Di Pasqua, A. J.; Miller, M. L.; Lu, X.; Peng, L.; Jay, M. Inorg.     Chim. Acta 2012, 393, 334. -   Bult, W.; Varkevisser, R.; Soulimani, F.; Seevinck, P. R.; De Leeuw,     H.; Bakker, C. J. G.; Luijten, P. R.; Van Het Schip, A. D.;     Hennink, W. E.; Nijsen, J. F. W. Pharm. Res. 2010, 27, 2205. -   Nijsen, J. F. W.; Zonnenberg, B. A.; Woittiez, J. R. W.; Rook, D.     W.; Swildens-Van Woudenberg, I. A.; Van Rijk, P. P.; Van het     Schip, A. D. Eur. J. Nucl. Med. 1999, 26, 699. -   Geldof, A. A.; Slotman, B. J. Cancer Lett. (Shannon, Irel) 1996,     101, 233. -   Rezaee, M.; Sanche, L.; Hunting, D. J. Radiat. Res. 2013, 179, 323. -   Hassan, M. I.; Sultana, N.; Hamdan, S. “Bioactivity Assessment of     Poly(ε-caprolactone)/Hydroxyapatite Electrospun Fibers for Bone     Tissue Engineering Application” J. Nanomater. 2014, 2014, 6. 

We claim:
 1. A iron garnet nanoparticle or iron garnet particle comprising one, or any combination of, activatable nuclide selected from lanthanum-139, praseodymium-141, samarium-152, dysprosium-164, holmium-165, rhenium-185 and or rhenium-187 and, optionally, comprising a radiosensitizer.
 2. The iron garnet nanoparticle or iron garnet particle according to claim 1, wherein said nanoparticle further comprises a radiosensitizer.
 3. The iron garnet nanoparticle or iron garnet particle according to claim 1, wherein said radiosensitizer comprises complexes containing platinum, ruthenium, palladium, iron, cobalt, nickel, copper, rhodium, gold, silver and/or boron or is selected from nitrous oxide, cisplatin, oxaliplatin and/or carboplatin.
 4. The iron garnet nanoparticle or iron garnet particle according to claim 1, wherein said nanoparticle further comprises a lipid or phospholipid coating.
 5. The iron garnet nanoparticle or iron garnet particle according to claim 4, wherein said lipid or phospholipid is selected from phosphatidic acid (phosphatidate) (PA), phosphatidylethanolamine (cephalin) (PE), phosphatidylcholine (lecithin) (PC), phosphatidylserine (PS), phosphoinositides, phosphatidylinositol (PI), phosphatidylinositol phosphate (PIP), phosphatidylinositol bisphosphate (PIP2), phosphatidylinositol triphosphate (PIP3), DDPC, DLPC, DMPC, DPPC, DSPC, DOPC, POPC, DRPC, DEPC and combinations thereof.
 6. The iron garnet nanoparticle or iron garnet particle according to claim 5, wherein said lipid or phospholipid is functionalized with a targeting agent and/or polyethylene glycol.
 7. The iron garnet nanoparticle or iron garnet particle according to claim 1, wherein said nanoparticle comprises the following ratios/ranges of to activatable radionuclide: about 40.0% to about 60.0% activatable nuclide containing IG and 0% to about 20% radiosensitizer; about 50.0% to about 60.0% activatable nuclide containing IG and 0% to about 12% radiosensitizer: about 50.0% to about 60.0% activatable nuclide containing IG and about 2.0% to about 7.0% radiosensitizer; about 50.0% to about 60.0% activatable nuclide containing IG and about 2.0% to about 12.0% radiosensitizer.
 8. The iron garnet nanoparticle according to claim 1, wherein said nanoparticles have a diameter of 0.1 to 100 nm, preferably 20-80 nm.
 9. An activated iron garnet nanoparticle or iron garnet particle according to claim 1, said activated iron garnet nanoparticle containing a radionuclide selected from lanthanum-142, praseodymium-142, samarium-153, dysprosium-165, holmium-166, rhenium-186 and/or rhenium-188 and optionally comprising a radiosensitizer.
 10. The activated iron garnet nanoparticle or iron garnet particle according to claim 9, wherein said nanoparticle is activated by neutron irradiation.
 11. The activated iron garnet nanoparticle or iron garnet particle according to claim 9, wherein said activated iron garnet nanoparticle emits radiation at subtherapeutic levels.
 12. The activated iron garnet nanoparticle or iron garnet particle according to claim 9, wherein said activated iron garnet nanoparticle emits radiation at therapeutic levels.
 13. The activated iron garnet nanoparticle or iron garnet particle according to claim 9, wherein said nanoparticle further comprises a radiosensitizer.
 14. The activated iron garnet nanoparticles or iron garnet particle according to claim 13, wherein said radiosensitizer is present in the following ratios/ranges of activated radionuclide to radiosensitizer (expressed as weight percent): about 40.0% to about 60.0% activated radionuclide containing IG and 0% to about 20% radiosensitizer; about 50.0% to about 60.0% activated radionuclide containing IG and 0% to about 12% radiosensitizer; about 50.0% to about 60.0% activated radionuclide containing IG and about 2.0% to about 7.0% radiosensitizer; or about 50.0% to about 60.0% activated radionuclide containing IG and about 2.0% to about 12.0% radiosensitizer.
 15. A film, electrospun fabric or bandage comprising an iron garnet nanoparticle or iron garnet particle according to claim 1 or an activated iron garnet nanoparticle.
 16. The film, electrospun fabric or bandage according to claim 15, wherein said film, electrospun fabric or bandage has relatively uniform distribution of said nanoparticles or particles within said film, electrospun fabric or bandage.
 17. The film, electrospun fabric or bandage according to claim 15, wherein said film, electrospun fabric or bandage emits relatively uniform radiation across the surface area of said film, electrospun fabric or bandage.
 18. The film, electrospun fabric or bandage according to claim 15, wherein said electrospun fabric comprises polymers selected from acrylonitriles, vinylimidazole, butyl acrylate, isoprene, butadiene, caprolactam and combinations thereof.
 19. The film, electrospun fabric or bandage according to claim 15, said film, electrospun fabric or bandage further comprising a wound healing agent or radiosensitizer.
 20. The film, electrospun fabric or bandage according to claim 19, wherein said wound healing agent is selected from antibiotics, anti-microbial agents, dialkylcarbamoylchloride, povidone-iodine, silver, growth factors, NO and combinations thereof and the radiosensitizer is platinum, ruthenium, palladium, iron, cobalt, nickel, copper, rhodium, gold, silver, NO, and/or boron.
 21. The film, electrospun fabric or bandage according to claim 20, wherein said wound healing agent is selected from epidermal growth factor (EGF), platelet derived growth factor (PDGF), fibroblast growth factor (FGF), transforming growth factor (TGF-β1), insulin-like growth factor (IGF-1), human growth hormone, granulocyte-macrophage colony-stimulating factor (GM-CSF) and combinations thereof.
 22. A pharmaceutical composition comprising a nanoparticle according to claim
 1. 23. A method of treating a disorder responsive to a radiotherapeutic agent to in a subject in need thereof, comprising administering to said subject a therapeutically effective amount of a nanoparticle or a particle according to claim 9, or a pharmaceutical composition thereof, to said subject.
 24. The method according to claim 23, wherein said disorder is a cancer.
 25. The method according to claim 23, wherein said disorder is selected from bacterial infections, viral infections, cancer, trigeminal neuralgia, severe thyroid eye disease, pterygium, pigmented villonodularsynovitis, vascular restenosis, heterotopic ossification and rheumatoid arthritis, synovial osteochondromatosis, synovial chondromatosis, a hematological cancer, acute myeloid leukemia, chronic myeloid leukemia, hairy cell leukemia, lymphoblastic leukemia, lymphocytic leukemia, AIDS-related lymphoma, Burkitt's lymphoma, cutaneous T-Cell lymphoma, Hodgkin lymphoma, Non-Hodgkin lymphoma, primary central nervous system lymphoma, myeloma, a solid cancer/tumor, anal cancer, basal cell carcinoma, bile duct cancer, bladder cancer, bone cancer, brain cancer, cerebellar astrocytoma, ependymoma, glioma, medulloblastoma, neuroblastoma, breast cancer, cervical cancer, colon cancer, endometrial cancer, esophageal cancer, eye cancer, gallbladder cancer, gastrointestinal cancer, heart cancer, renal cell carcinoma, laryngeal cancer, lip cancer, liver cancer, lung cancer, melanoma, mesothelioma, oral cancer, ovarian cancer, pancreatic cancer, parathyroid cancer, peritoneal carcinomatosis, pharyngeal cancer, prostate cancer, rectal cancer, skin cancer, stomach cancer, throat cancer, thyroid cancer, urethral cancer, uterine cancer, vaginal cancer or vulvar cancer.
 26. A method of identifying the site of a disorder in a subject in need thereof, comprising administering to said subject an amount of a nanoparticle or particle according to claim 9, or a pharmaceutical composition thereof, to said subject, said amount of nanoparticle or particle emitting radiation detectable by an imaging technique selected from magnetic resonance imaging (MRI), X ray computed tomography (CT), Single Photon Emission Computed Tomography (SPECT) and micro-computed tomography (MicroCT).
 27. The method according to claim 26, wherein said disorder is a cancer.
 28. The method according to claim 26, wherein said disorder is selected from bacterial infections, viral infections, cancer, trigeminal neuralgia, severe thyroid eye disease, pterygium, pigmented villonodularsynovitis, vascular restenosis, heterotopic ossification and rheumatoid arthritis, synovial osteochondromatosis, synovial chondromatosis, a hematological cancer, acute myeloid leukemia, chronic myeloid leukemia, hairy cell leukemia, lymphoblastic leukemia, lymphocytic leukemia, AIDS-related lymphoma, Burkitt's lymphoma, cutaneous T-Cell lymphoma, Hodgkin lymphoma, Non-Hodgkin lymphoma, primary central nervous system lymphoma, myeloma, a solid cancer/tumor, anal cancer, basal cell carcinoma, bile duct cancer, bladder cancer, bone cancer, brain cancer, cerebellar astrocytoma, ependymoma, glioma, medulloblastoma, neuroblastoma, breast cancer, cervical cancer, colon cancer, endometrial cancer, esophageal cancer, eye cancer, gallbladder cancer, gastrointestinal cancer, heart cancer, renal cell carcinoma, laryngeal cancer, lip cancer, liver cancer, lung cancer, melanoma, mesothelioma, oral cancer, ovarian cancer, pancreatic cancer, parathyroid cancer, peritoneal carcinomatosis, pharyngeal cancer, prostate cancer, rectal cancer, skin cancer, stomach cancer, throat cancer, thyroid cancer, urethral cancer, uterine cancer, vaginal cancer or vulvar cancer and said nanoparticle is functionalized with an antibody or receptor ligand that interacts with the surface of a cell associated with or causing said disorder.
 29. A method of treating a skin disease or condition comprising the application of a film, electrospun fabric or bandage comprising an activated iron garnet nanoparticle or activated iron garnet particle according to claim 9 to the skin of a subject having a skin disease or condition.
 30. The method according to claim 29, wherein said film, electrospun fabric or bandage has relatively uniform distribution of said nanoparticles within said film, electrospun fabric or bandage.
 31. The method according to claim 29, wherein said film, electrospun fabric or bandage emits relatively uniform radiation across the surface area of said film, electrospun fabric or bandage.
 32. The method according to claim 29, wherein said electrospun fabric comprises polymers selected from acrylonitriles, vinylimidazole, butyl acrylate, isoprene, butadiene, caprolactam and combinations thereof.
 33. The method according to claim 29, wherein the film, electrospun fabric or bandage further comprising a wound healing agent or a radiosensitizer.
 34. The method according to claim 33, wherein said wound healing agent is selected from antibiotics, anti-microbial agents, dialkylcarbamoylchloride, povidone-iodine, silver, growth factors, NO and combinations thereof and the radiosensitizer is platinum, ruthenium, palladium, iron, cobalt, nickel, copper, rhodium, gold, silver, NO, and/or boron.
 35. The method according to claim 33, wherein said wound healing agent is selected from epidermal growth factor (EGF), platelet derived growth factor (PDGF), fibroblast growth factor (FGF), transforming growth factor (TGF-β1), insulin-like growth factor (IGF-1), human growth hormone, granulocyte-macrophage colony-stimulating factor (GM-CSF) and combinations thereof.
 36. The method according to claim 29, wherein said skin disease or disorder is selected from psoriasis, skin cancer, melanoma, Merkel cell carcinoma, or squamous cell carcinoma.
 37. The method according to claim 23, wherein said nanoparticle or particle is magnetically guided to a target site. 